Al substitution in MgB2 crystals: influence on superconducting and structural properties

Abstract

Single crystals of Mg1-xAlxB2 have been grown at a pressure of 30 kbar using the cubic anvil technique. Precipitation free crystals with x < 0.1 were obtained as a result of optimization of already developed MgB2 crystal growth procedure. Systematic decrease of the c-axis lattice constant with increasing Al content, when the a-axis lattice constant is practically unchanged, was observed. Variation of the critical temperature on Al content in Mg1-xAlxB2 crystals was found to be slightly different than that one observed for polycrystalline samples since, even a very small substitution of 1-2% of Al leads to the decrease of Tc by about 2-3 K. X-ray and high resolution transmission electron microscopy investigations indicate on the appearance of second precipitation phase in the crystals with x > 0.1. This is in a form of non-superconducting MgAlB4 domains in the structure of superconducting Mg1-xAlxB2 matrix. Resistivity and magnetic investigations show the slight increase of the upper critical field, Hc2, for H//c for the samples with small x, significant reduction of the Hc2 anisotropy at lower temperatures, and decrease of the residual resistance ratio value for Al substituted samples as compared to those of unsubstituted crystals. Superconducting gaps variation as a function of Al content, investigated with point contact spectroscopy for the series of the crystals with Tc in the range from 20 to 37 K, does not indicate on the merging of the gaps with decreasing Tc down to 20 K. It may be related to an appearance of the precipitation phase in the Mg1-xAlxB2 structure.