Alloyed B-(AlxGa1-x)2O3 bulk Czochralski single B-(Al0.1Ga0.9)2O3 and polycrystals B-(Al0.33Ga0.66)2O3, B-(Al0.5Ga0.5)2O3), and property trends

In this work, bulk Czochralski-grown single crystals of 10 mol. % Al2O3 alloyed B-Ga2O3 - monoclinic 10% AGO or B-(Al0.1Ga0.9)2O3 - are obtained, which show +0.20 eV increase in the bandgap compared with unintentionally doped B-Ga2O3. Further, growths of 33% AGO - B-(Al0.33Ga0.67)2O3 - and 50% AGO - B-(Al0.5Ga0.5)2O3 or B-AlGaO3 - produce polycrystalline single-phase monoclinic material (B-AGO). All three compositions are investigated by x-ray diffraction, Raman spectroscopy, optical absorption, and 27Al nuclear magnetic resonance (NMR). By investigating single phase B-AGO over a large range of Al2O3 concentrations (10 - 50 mol. %), broad trends in the lattice parameter, vibrational modes, optical bandgap, and crystallographic site preference are determined. All lattice parameters show a linear trend with Al incorporation. According to NMR, aluminum incorporates on both crystallographic sites of B-Ga2O3, with a slight preference for the octahedral (GaII) site, which becomes more disordered with increasing Al. Single crystals of 10% AGO were also characterized by x-ray rocking curve, transmission electron microscopy, purity (glow discharge mass spectroscopy and x-ray fluorescence), optical transmission (200 nm - 20 um wavelengths), and resistivity. These measurements suggest that electrical compensation by impurity acceptor doping is not the likely explanation for high resistivity, but rather the shift of a hydrogen level from a shallow donor to a deep acceptor due to Al alloying. .. Cont. This article may be downloaded for personal use only. Any other use requires prior permission of the author and AIP Publishing. This article appeared in Journal of Applied Physics 131 155702.

cond-mat.mtrl-sci

Growth and Characterization of Metalorganic Vapor-Phase Epitaxy-Grown \b{eta}-(AlxGa1-x)2O3/\b{eta}-Ga2O3 Heterostructure Channels

We report on the growth and characterization of metalorganic vapor-phase epitaxy-grown \b{eta}-(AlxGa1-x)2O3/\b{eta}-Ga2O3 modulation-doped heterostructures. Electron channel is realized in the heterostructure by utilizing a delta-doped \b{eta}-(AlxGa1-x)2O3 barrier. Electron channel characteristics are studied using transfer length method, capacitance-voltage and Hall measurements. Hall sheet charge density of 1.06 x 1013 cm-2 and mobility of 111 cm2/Vs is measured at room temperature. Fabricated transistor showed peak current of 22 mA/mm and on-off ratio of 8 x 106. Sheet resistance of 5.3 kΩ/Square is measured at room temperature, which includes contribution from a parallel channel in \b{eta}-(AlxGa1-x)2O3.

physics.app-ph

Delta-doped \b{eta}-Ga2O3 Films With Low FWHM Charge Profile Grown By Metalorganic Vapor-Phase Epitaxy

We report on low-temperature MOVPE growth of silicon delta-doped \b{eta}-Ga2O3 films with low FWHM. The as-grown films are characterized using Secondary-ion mass spectroscopy, Capacitance-Voltage and Hall techniques. SIMS measurements show that surface segregation is the chief cause of large FWHM in MOVPE-grown films. The surface segregation coefficient (R) is observed to reduce with reduction in the growth temperature. Films grown at 600 °C show an electron concentration of 9.7 x 1012 cm-2 and a FWHM of 3.2 nm. High resolution scanning/transmission electron microscopy of the epitaxial film did not reveal any significant observable degradation in crystal quality of the delta sheet and surrounding regions. Hall measurements of delta-doped film on Fe-doped substrate showed a sheet charge density of 6.1 x 1012 cm-2 and carrier mobility of 83 cm2/V. s. Realization of sharp delta doping profiles in MOVPE-grown \b{eta}-Ga2O3 is promising for high performance device applications.

physics.app-ph