Polarity-induced selective area epitaxy of GaN nanowires

We present a conceptually novel approach to achieve selective area epitaxy of GaN nanowires. The approach is based on the fact that these nanostructures do not form in plasma-assisted molecular beam epitaxy on structurally and chemically uniform cation-polar substrates. By in situ depositing and nitridating Si on a Ga-polar GaN film, we locally reverse the polarity to induce the selective area epitaxy of N-polar GaN nanowires. We show that the nanowire number density can be controlled over several orders of magnitude by varying the amount of pre-deposited Si. Using this growth approach, we demonstrate the synthesis of single-crystalline and uncoalesced nanowires with diameters as small as 20 nm. The achievement of nanowire number densities low enough to prevent the shadowing of the nanowire sidewalls from the impinging fluxes paves the way for the realization of homogeneous core-shell heterostructures without the need of using ex situ pre-patterned substrates.

physics.app-ph

Ferromagnet/Semiconductor/Ferromagnet Hybrid Trilayers grown using solid phase epitaxy

The direct growth of semiconductors over metals by molecular beam epitaxy is a difficult task due to the large differences in crystallization energy between these types of materials. This aspect is problematic in the context of spintronics, where coherent spin-injection must proceed via ballistic transport through sharp interfacial Schottky barriers. We report the realization of single-crystalline ferromagnet/semiconductor/ferromagnet hybrid trilayers using solid-phase epitaxy, with combinations of Fe3Si, Co2FeSi, and Ge. The slow annealing of amorphous Ge over Fe3Si results in a crystalline filmlm identified as FeGe2. When the annealing is performed over Co2FeSi, reflected high-energy electron diffraction and X-ray diffraction indicate the creation of a different crystalline Ge(Co,Fe,Si) compound, which also preserves growth orientation. It was possible to observe independent magnetization switching of the ferromagnetic layers in a Fe3Si/FeGe2/Co2FeSi sample, thanks to the different coercive fields of the two metals and to the quality of the interfaces. This result is a step towards the implementation of vertical spin-selective transistor-like devices.

cond-mat.mtrl-sci

Elastic vs. plastic strain relaxation in coalesced GaN nanowires: an x-ray diffraction study

The coalescence in dense arrays of spontaneously formed GaN nanowires proceeds by bundling: adjacent nanowires bend and merge at their top, thus reducing their surface energy at the expense of the elastic energy of bending. We give a theoretical description of the energetics of this bundling process. The bending energy is shown to be substantially reduced by the creation of dislocations at the coalescence joints. A comparison of experimental and calculated x-ray diffraction profiles from ensembles of bundled nanowires demonstrates that a large part of the bending energy is indeed relaxed by plastic deformation. The residual bending manifests itself by extended tails of the diffraction profiles.

cond-mat.mtrl-sci

Diffraction at GaAs/Fe$_{3}$Si core/shell nanowires: the formation of nanofacets

GaAs/Fe$_{3}$Si core/shell nanowire structures were fabricated by molecular-beam epitaxy on oxidized Si(111) substrates and investigated by synchrotron x-ray diffraction. The surfaces of the Fe$_3$Si shells exhibit nanofacets. These facets consist of well pronounced Fe$_3$Si{111} planes. Density functional theory reveals that the Si-terminated Fe$_3$Si{111} surface has the lowest energy in agreement with the experimental findings. We can analyze the x-ray diffuse scattering and diffraction of the ensemble of nanowires avoiding the signal of the substrate and poly-crystalline films located between the wires. Fe$_3$Si nanofacets cause streaks in the x-ray reciprocal space map rotated by an azimuthal angle of 30° compared with those of bare GaAs nanowires. In the corresponding TEM micrograph the facets are revealed only if the incident electron beam is oriented along [1$\overline{1}$0] in accordance with the x-ray results. Additional maxima in the x-ray scans indicate the onset of chemical reactions between Fe$_{3}$Si shells and GaAs cores occurring at increased growth temperatures.

cond-mat.mtrl-sci

Structure of Fe3Si/Al/Fe3Si thin film stacks on GaAs(001)

Fe3Si/Al/Fe3Si/GaAs(001) structures were deposited by molecular-beam epitaxy and characterized by transmission and scanning electron microscopy, and x-ray diffraction. The first Fe3Si film on GaAs(001) is growing epitaxially as (001) oriented single crystal. The subsequent Al film grows almost 111 oriented in a fibre texture although the underlying Fe3Si is exactly (001) oriented. The growth in this orientation is triggered by a thin transition region which is formed at the Fe3Si/Al interface. In the end after the growth of the second Fe3Si layer on top of the Al the final properties of the whole stack depend on the substrate temperature T_S during deposition of the last film. The upper Fe3Si films are mainly 110 oriented although they are poly-crystalline. At lower T_S, around room temperature, all the films retain their original structural properties.

cond-mat.mtrl-sci

Facetted growth of Fe3Si shells around GaAs nanowires on Si(111)

GaAs nanowires and GaAs/Fe3Si core/shell nanowire structures were grown by molecular-beam epitaxy on oxidized Si(111) substrates and characterized by transmission electron microscopy. The surfaces of the original GaAs NWs are completely covered by magnetic Fe3Si exhibiting nanofacets and an enhanced surface roughness compared to the bare GaAs NWs. Shell growth at a substrate temperature of T{S} = 200 °C leads to regular nanofacetted Fe3Si shells. These facets, which lead to thickness inhomogeneities of the shells, consist mainly of well pronounced Fe3Si(111) planes. The crystallographic orientation of core and shell coincide, i.e. they are pseudomorphic. The nanofacetted Fe3Si shells found in the present work are probably the result of the Vollmer-Weber island growth mode of Fe3Si on the {110} side facets of the GaAs NWs.

cond-mat.mtrl-sci

Real structure of lattice matched GaAs-Fe3Si core-shell nanowires

GaAs nanowires and GaAs-Fe3Si core-shell nanowire structures were grown by molecular-beam epitaxy on oxidized Si(111) substrates and characterized by transmission electron microscopy (TEM) and X-ray diffraction (XRD). Ga droplets were formed on the oxide surface, and the semiconducting GaAs nanowires grew epitaxially via the vapor-liquid-solid mechanism as single-crystals from holes in the oxide film. We observed two stages of growth of the GaAs nanowires, first the regular growth and second the residual growth after the Ga supply was finished. The magnetic Fe3Si shells were deposited in an As-free chamber. They completely cover the GaAs cores although they consist of small grains. High-resolution TEM micrographs depict the differently oriented grains in the Fe3Si shells. Selected area diffraction of electrons and XRD gave further evidence that the shells are textured and not single crystals. Facetting of the shells was observed, which lead to thickness inhomogeneities of the shells.

cond-mat.mtrl-sci

Spatially resolved investigation of strain and composition variations in (In,Ga)N/GaN epilayers

The strain state and composition of a 400 nm thick (In,Ga)N layer grown by metal-organic chemical vapor deposition on a GaN template are investigated by spatially integrated x-ray diffraction and cathodoluminescence (CL) spectroscopy as well as by spatially resolved CL and energy dispersive x-ray analysis. The CL investigations confirm a process of strain relaxation accompanied by an increasing indium content toward the surface of the (In,Ga)N layer, which is known as the compositional pulling effect. Moreover, we identify the strained bottom, unstrained top, and gradually relaxed intermediate region of the (In,Ga)N layer. In addition to an increase of the indium content along the growth direction, the strain relaxation leads to an enhancement of the lateral variations of the indium distribution toward the surface.

cond-mat.mtrl-sci

Macro- and micro-strain in GaN nanowires on Si(111)

We analyze the strain state of GaN nanowire ensembles by x-ray diffraction. The nanowires are grown by molecular beam epitaxy on a Si(111) substrate in a self-organized manner. On a macroscopic scale, the nanowires are found to be free of strain. However, coalescence of the nanowires results in micro-strain with a magnitude from +-0.015% to +-0.03%.This micro-strain contributes to the linewidth observed in low-temperature photoluminescence spectra.

cond-mat.mes-hall

Residual disorder and diffusion in thin Heusler alloy films

Co2FeSi/GaAs(110) and Co2FeSi/GaAs(111)B hybrid structures were grown by molecular-beam epitaxy and characterized by transmission electron microscopy (TEM) and X-ray diffraction. The films contained inhomogeneous distributions of ordered L2_1 and B2 phases. The average stoichiometry was controlled by lattice parameter measurements, however diffusion processes lead to inhomogeneities of the atomic concentrations and the degradation of the interface, influencing long-range order. An average long-range order of 30-60% was measured by grazing-incidence X-ray diffraction, i.e. the as-grown Co2FeSi films were highly but not fully ordered. Lateral inhomogeneities of the spatial distribution of long-range order in Co2FeSi were found using dark-field TEM images taken with superlattice reflections.

cond-mat.mes-hall

Luminescence of GaAs nanowires consisting of wurtzite and zincblende segments

GaAs nanowires (NWs) grown by molecular-beam epitaxy may contain segments of both the zincblende (ZB) and wurtzite (WZ) phases. Depending on the growth conditions, we find that optical emission of such NWs occurs either predominantly above or below the band gap energy of ZB GaAs [E(g,ZB)]. This result is consistent with the assumption that the band gap energy of wurtzite GaAs [E(g,WZ)] is larger than E(g,ZB) and that GaAs NWs with alternating ZB and WZ segments along the wire axis establish a type II band alignment, where electrons captured within the ZB segments recombine with holes of the neighboring WZ segments. Thus, the corresponding transition energy depends on the degree of confinement of the electrons, and transition energies exceeding E(g,ZB) are possible for very thin ZB segments. At low temperatures, the incorporation of carbon acceptors plays a major role in determining the spectral profile as these can effectively bind holes in the ZB segments. From cathodoluminescence measurements of single GaAs NWs performed at room temperature, we deduce a lower bound of 55 meV for the difference E(g,WZ)-E(g,ZB).

cond-mat.mtrl-sci

In situ x-ray diffraction study of epitaxial growth of ordered Fe3Si films

Molecular beam epitaxy of Fe3Si on GaAs(001) is studied in situ by grazing incidence x-ray diffraction. Layer-by-layer growth of Fe3Si films is observed at a low growth rate and substrate temperatures near 200 degrees Celsius. A damping of x-ray intensity oscillations due to a gradual surface roughening during growth is found. The corresponding sequence of coverages of the different terrace levels is obtained. The after-deposition surface recovery is very slow. Annealing at 310 degrees Celsius combined with the deposition of one monolayer of Fe3Si restores the surface to high perfection and minimal roughness. Our stoichiometric films possess long-range order and a high quality heteroepitaxial interface.

cond-mat.mtrl-sci