D. W. Boukhvalov

Publications and source records attributed to D. W. Boukhvalov.

At least 19 recordsLinked to original sources
arXiv2024

Structural, electronic, and optical properties of 6H-SiC layers synthesized by implantation of carbon ions into silicon

Systematic studies of the gradual fabrication by means of carbon ion-implantation of high-quality 6H-SiC layers on silicon surfaces have been carried out. The fluence of carbon ions varied from 5*10^15 cm-2 to 10^17 cm-2. Results of first-principle calculations, X-ray diffraction (XRD), and Raman spectroscopy demonstrate the amorphization of silicon substrate without any tendency to the segregation of carbon in the samples synthesized at low fluencies. The formation of a SiO2-like structure at this stage was also detected. X-ray photoelectron spectroscopy (XPS), XRD, and Raman spectroscopy demonstrate that an increase in carbon content at 10^17 cm-2 fluence leads to the growth of 6H-SiC films on the surface of the amorphous silicon substrate. Atomic force microscopy (AFM) data obtained also demonstrates the decreasing of surface roughens after the formation of SiC film. XPS and Raman spectra suggest that excessive carbon content leaves the SiC matrix via the formation of an insignificant amount of partially oxidized carbon nanostructures. Optical measurements also support the claim of high-quality 6H-SiC film formation in the samples synthesized at 10^17 cm-2 fluence and demonstrate the absence of any detectable contribution of nanostructures formed from excessive carbon on the optical properties of the material under study.

cond-mat.mtrl-sci↗
arXiv2024

Formation of yttrium oxalate phase filled by carbon clusters on the surface of yttrium oxide films

In the current paper, we report the results of surface modification of cubic Y2O3 films employing carbon-ion implantation. The characterization results demonstrate the formation of a stable yttrium oxalate-based structure with cavities filled with carbon clusters. Theoretical simulations demonstrate that the incorporation of eighteen-atom carbon clusters into the cavities of Y2(C2O4)3 does not lead to valuable changes in the crystal structure of yttrium oxalate. X-ray diffraction and optical measurements demonstrate that the subsurface bulk area of cubic yttrium oxide remains unperturbed. The oxalate "skin" thickness with embedded carbon clusters is estimated to be approximately 10 nm. The prospective employing the method to manage optical properties and increase the biocompatibility of yttria and lanthanide oxides are discussed.

cond-mat.mtrl-sci↗
arXiv2023

Uncommon 2D Diamond-like Carbon Nanodots Derived from Nanotubes: Atomic Structure, Electronic States and Photonic Properties

In this article, we report the results of relatively facile fabrication of carbon nanodots from single-walled and multi-walled carbon nanotubes (SWCNT and MWCNT). The results of X-ray photoelectron spectroscopy (XPS) and Raman measurements show that the obtained carbon nanodots are quasi-two-dimensional objects with a diamond-like structure. Based on the characterization results, a theoretical model of synthesized carbon nanodots was developed. The measured absorption spectra demonstrate the similarity of the local atomic structure of carbon nanodots synthesized from single-walled and multi-walled carbon nanotubes. However, the photoluminescence (PL) spectra of nanodots synthesized from both sources turned out to be completely different. Carbon dots fabricated from MWCNTs exhibit PL spectra similar to nanoscale carbon systems with sp3 hybridization and a valuable edge contribution. At the same time nanodots synthesized from SWCNTs exhibit PL spectra which are typical for quantum dots with an estimated size of ~0.6-1.3 nm.

cond-mat.mes-hall↗
arXiv2022

Comparative Analysis of the Electronic Energy Structure of Nanocrystalline Polymorphs of Y2O3 Thin Layers: Theory and Experiments

The results of fabrication and characterization of atomic structure of nanocrystalline thin layers of Y2O3 in cubic and monoclinic phases is reported. Experimental data demonstrate crystalline ordering in nanocrystalline films with average grain size of ~10-14 nm both for cubic and monoclinic studied structures. Density Functional Theory (DFT) based simulations demonstrate insignificant differences of electronic structure of these phases in the bulk and on the surfaces. Theoretical modeling also pointed out the significant broadening of valence and conductive bands caused by means of energy levels splitting in agreement with experimental data (X-ray photoelectron and photoluminescence spectra). The presence of various intrinsic and extrinsic defects (including surface adsorption of carbon mono- and dioxide) does not promote visible changes in electronic structure of Y2O3 surface for both studied phases. Optical absorption and luminescence measurements indicate insignificant bandgap reduction of Y2O3 nanocrystalline layers and the very little contribution from defect states. Simulation of extrinsic compression and expanding demonstrate stability of the electronic structure of nanocrystalline Y2O3 even under significant strain. Results of comprehensive studies demonstrate that yttrium oxide based nanocrystalline layers are prospective for various optical applications as a stable material.

cond-mat.mtrl-sci↗
arXiv2022

A Comprehensive Model of Nitrogen-Free Ordered Carbon Quantum Dots

We propose and demonstrate a novel range of models to accurately determine the optical properties of nitrogen-free carbon quantum dots (CQDs) with ordered graphene layered structures. We confirm the results of our models against the full range of experimental results for CQDs available from an extensive review of the literature. The models can be equally applied to CQDs with varied sizes and with different oxygen content in the basal planes of the constituent graphenic sheets. We demonstrate that the experimentally observed blue fluorescent emission of nitrogen-free CQDs can be associated with either small oxidised areas on the periphery of the graphenic sheets, or with sub-nanometre non-functionalised islands of sp2-hybridised carbon with high symmetry confined in the centres of oxidised graphene sheets. Larger and/or less symmetric non-functionalised regions in the centre of functionalised graphene sheet are found to be sources of green and even red fluorescent emission from nitrogen-free CQDs. We also demonstrate an approach to simplify the modelling of the discussed sp2-islands by substitution with equivalent strained polycyclic aromatic hydrocarbons. Additionally, we show that the bandgaps (and photoluminescence) of CQDs are not dependent on either out-of-plane corrugation of the graphene sheet or the spacing between sp2-islands. Advantageously, our proposed models show that there is no need to involve light-emitting polycyclic aromatic molecules (nanographenes) with arbitrary structures grafted to the particle periphery to explain the plethora of optical phenomena observed for CQDs across the full range of experimental works.

cond-mat.mes-hall↗
arXiv2020

Uncommon clustering in dilute Ti-Fe alloys

We present the results of ab initio modeling of structure of dilute Ti-Fe, a typical representative of quenched Ti-based transition-metal alloys. We have demonstrated that beyond the solubility limit this alloy cannot be described in common terms of substitutional and interstitial alloys. Instead, very stable local clusters are formed in both low-temperature hcp and high-temperature bcc phases of alloys, with almost identical local structures. This gives an example of geometrically frustrated state and explains unusual concentration behavior of Mössbauer spectra discovered long ago for this system.

cond-mat.mtrl-sci↗
arXiv2019

Fundamental Crystal Field Excitations in Magnetic Semiconductor SnO$_2$:Mn,Fe,Co,Ni

Directly measuring elementary electronic excitations in dopant $3d$ metals is essential to understanding how they function as part of their host material. Through calculated crystal field splittings of the $3d$ electron band it is shown how transition metals Mn, Fe, Co, and Ni are incorporated into SnO$_2$. The crystal field splittings are compared to resonant inelastic x-ray scattering (RIXS) experiments, which measure precisely these elementary $dd$ excitations. The origin of spectral features can be determined and identified via this comparison, leading to an increased understanding of how such dopant metals situate themselves in, and modify the host's electronic and magnetic properties; and also how each element differs when incorporated into other semiconducting materials. We found that oxygen vacancy formation must not occur at nearest neighbour sites to metal atoms, but instead must reside at least two coordination spheres beyond. The coordination of the dopants within the host can then be explicitly related to the $d$-electron configurations and energies. This approach facilitates an understanding of the essential link between local crystal coordination and electronic/magnetic properties.

cond-mat.mtrl-sci↗
arXiv2018

The role of surface chemical reactivity in the stability of electronic nanodevices based on two-dimensional materials "beyond graphene" and topological insulators

Here, we examine the influence of surface chemical reactivity toward ambient gases on the performance of nanodevices based on two-dimensional materials "beyond graphene" and novel topological phases of matter. While surface oxidation in ambient conditions was observed for silicene and phosphorene with subsequent reduction of the mobility of charge carriers, nanodevices with active channels of indium selenide, bismuth chalcogenides and transition-metal dichalcogenides are stable in air. However, air-exposed indium selenide suffers of p-type doping due to water decomposition on Se vacancies, whereas the low mobility of charge carriers in transition-metal dichalcogenides increases the response time of nanodevices. Conversely, bismuth chalcogenides require a control of crystalline quality, which could represent a serious hurdle for up scaling.

cond-mat.mtrl-sci↗
arXiv2018

Stability of boron-doped graphene/copper interface: DFT, XPS and OSEE studies

Two different types of boron-doped graphene/copper interfaces synthesized using two different flow rates of Ar through the bubbler containing the boron source were studied. X-ray photoelectron spectra (XPS) and optically stimulated electron emission (OSEE) measurements have demonstrated that boron-doped graphene coating provides a high corrosion resistivity of Cu-substrate with the light traces of the oxidation of carbon cover. The density functional theory calculations suggest that for the case of substitutional (graphitic) boron-defect only the oxidation near boron impurity is energetically favorable and creation of the vacancies that can induce the oxidation of copper substrate is energetically unfavorable. In the case of non-graphitic boron defects oxidation of the area, a nearby impurity is metastable that not only prevent oxidation but makes boron-doped graphene. Modeling of oxygen reduction reaction demonstrates high catalytic performance of these materials.

cond-mat.mtrl-sci↗
arXiv2017

Electronic structure, charge transfer, and intrinsic luminescence of gadolinium oxide nanoparticles: Experiment and theory

The cubic (c) and monoclinic (m) polymorphs of Gd2O3 were studied using the combined analysis of several materials science techniques - X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and photoluminescence (PL) spectroscopy. Density functional theory (DFT) based calculations for the samples under study were performed as well. The cubic phase of gadolinium oxide (c-Gd2O3) synthesized using a precipitation method exhibits spheroidal-like nanoclusters with well-defined edges assembled from primary nanoparticles with an average size of 50 nm, whereas the monoclinic phase of gadolinium oxide (m-Gd2O3) deposited using explosive pyrolysis has a denser structure compared with natural gadolinia. This phase also has a structure composed of three-dimensional complex agglomerates without clear-edged boundaries that are ~21 nm in size plus a cubic phase admixture of only 2 at. % composed of primary edge-boundary nanoparticles ~15 nm in size. These atomic features appear in the electronic structure as different defects ([Gd...O-OH] and [Gd...O-O]) and have dissimilar contributions to the charge-transfer processes among the appropriate electronic states with ambiguous contributions in the Gd 5p - O 2s core-like levels in the valence band structures. The origin of [Gd...O-OH] defects found by XPS was well-supported by PL analysis. The electronic and atomic structures of the synthesized gadolinias calculated using DFT were compared and discussed on the basis of the well-known joint OKT-van der Laan model, and good agreement was established.

cond-mat.mes-hall↗
arXiv2017

Atomic and electronic structures of stable linear carbon chains on Ag-nanoparticles

In this work, we report X-ray photoelectron (XPS) and valence band (VB) spectroscopy measurements of surfactant-free silver nanoparticles and silver/linear carbon chains (Ag@LCC) structures prepared by pulse laser ablation (PLA) in water. Our measurements demonstrate significant oxidation only on the surfaces of the silver nanoparticles with many covalent carbon-silver bonds but only negligible traces of carbon-oxygen bonds. Theoretical modeling also provides evidence of the formation of robust carbon-silver bonds between linear carbon chains and pure and partially oxidized silver surfaces. A comparison of theoretical and experimental electronic structures also provides evidence of the presence of non-oxidized linear carbon chains on silver surfaces. To evaluate the chemical stability, we investigated the energetics of the physical adsorption of oxidative species (water and oxygen) and found that this adsorption is much preferrable on oxidized or pristine silver surfaces than the adsorption of linear carbon chains, which makes the initial step in the oxidation of LCC energetically unfavorable.

cond-mat.mes-hall↗
arXiv2017

The MRO-accompanied modes of Re-implantation into SiO2-host matrix: XPS and DFT based scenarios

The following scenarios of Re-embedding into SiO2-host by pulsed Re-implantation were derived and discussed after XPS-and-DFT electronic structure qualification: (i) low Re-impurity concentration mode -> the formation of combined substitutional and interstitial impurities with Re2O7-like atomic and electronic structures in the vicinity of oxygen vacancies; (ii) high Re-impurity concentration mode -> the fabrication of interstitial Re-metal clusters with the accompanied formation of ReO2-like atomic structures and (iii) an intermediate transient mode with Re-impurity concentration increase, when the precursors of interstitial defect clusters are appeared and growing in the host-matrix structure occur. An amplification regime of Re-metal contribution majority to the final Valence Band structure was found as one of the sequences of intermediate transient mode. It was shown that most of the qualified and discussed modes were accompanied by the MRO (middle range ordering) distortions in the initial oxygen subnetwork of the a-SiO2 host-matrix because of the appeared mixed defect configurations.

cond-mat.mtrl-sci↗
arXiv2017

Atomic and electronic structure of a copper/graphene interface as prepared and 1.5 years after

We report the results of X-ray spectroscopy and Raman measurements of as-prepared graphene on a high quality copper surface and the same materials after 1.5 years under different conditions (ambient and low humidity). The obtained results were compared with density functional theory calculations of the formation energies and electronic structures of various structural defects in graphene/Cu interfaces. For evaluation of the stability of the carbon cover, we propose a two-step model. The first step is oxidation of the graphene, and the second is perforation of graphene with the removal of carbon atoms as part of the carbon dioxide molecule. Results of the modeling and experimental measurements provide evidence that graphene grown on high-quality copper substrate becomes robust and stable in time (1.5 years). However, the stability of this interface depends on the quality of the graphene and the number of native defects in the graphene and substrate. The effect of the presence of a metallic substrate with defects on the stability and electronic structure of graphene is also discussed.

cond-mat.mtrl-sci↗
arXiv2017

Enhanced clustering tendency of Cu-impurities with a number of oxygen vacancies in heavy carbon-loaded TiO2 - the bulk and surface morphologies

The over threshold carbon-loadings (~50 at.%) of initial TiO2-hosts and posterior Cu-sensitization (~7 at.%) was made using pulsed ion-implantation technique in sequential mode with 1 hour vacuum-idle cycle between sequential stages of embedding. The final Cx-TiO2:Cu samples were qualified using XPS wide-scan elemental analysis, core-levels and valence band mappings. The results obtained were discussed on the theoretic background employing DFT-calculations. The combined XPS and DFT analysis allows to establish and prove the final formula of the synthesized samples as Cx-TiO2:[Cu+][Cu2+] for the bulk and Cx-TiO2:[Cu+][Cu0] for thin-films. It was demonstrated the in the mode of heavy carbon-loadings the remaining majority of neutral C-C bonds (sp3-type) is dominating and only a lack of embedded carbon is fabricating the O-C=O clusters. No valence base-band width altering was established after sequential carbon-copper modification of the atomic structure of initial TiO2-hosts except the dominating majority of Cu 3s states after Cu-sensitization. The crucial role of neutral carbon low-dimensional impurities as the precursors for the new phases growth was shown for Cu-sensitized Cx-TiO2 intermediate-state hosts.

cond-mat.mtrl-sci↗
arXiv2017

Development of theoretical descriptors for cytotoxicity evaluation of metallic nanoparticles

Motivated by the recent development of quantitative structure-activity relationship (QSAR) methods in the area of nanotoxicology, we proposed an approach to develop additional descriptors based on results of first principles calculations. For evaluation of the biochemical activity of metallic nanoparticles, we consider two processes: ion extraction from the surface of a specimen to aqueous media and water dissociation on the surface. We performed calculations for a set of metals (Al, Fe, Cu, Ag, Au, Pt). Taking into account the diversity of atomic structures of real metallic nanoparticles, we performed calculations for different models such as (001) and (111) surfaces, nanorods, and two different cubic nanoparticles of 0.6 and 0.3 nm size. Significant energy dependence of the processes from the selected model of nanoparticle suggests that for the correct description we should combine the calculations for the several representative models. In addition to the descriptors of chemical activity of the metallic nanoparticles for the two studied processes, we propose descriptors for taking into account the dependence of chemical activity from the size and shape of nanoparticles. Routes to minimization of computational costs for these calculations are also discussed.

cond-mat.mes-hall↗
arXiv2016

XPS and DFT study of pulsed Bi-implantation of bulk and thin-films of ZnO - the role of oxygen imperfections

An atomic and electronic structure of the bulk and thin-film morphologies of ZnO were modified using pulsed Bi-ion implantation (1x1017 cm-2 fluence, 70 min exposure under Bi-ion beam, EBi+ = 30 keV, pulsed ion-current density of not more than 0.8 mA/cm2 with a repetition rate of 12.5 Hz). The final samples were qualified by X-ray photoelectron core-level and valence band mapping spectroscopy applying ASTM materials science standard. The spectroscopy data obtained was discussed on the basis of DFT-models for Bi-embedding into ZnO host-matrices. It was established that in the case of direct Bi-impurities insertion into the employed ZnO-host for both studied morphologies neither the only "pure" Bi2O3-like phase nor the only "pure" Bi-metal will be preferable to appear as a secondary phase. An unfavorability of the large cluster agglomeration of Bi-impurities in ZnO-hosts has been shown and an oxygen 2s electronic states pleomorphizm was surely established.

cond-mat.mtrl-sci↗
arXiv2016

Charge transfer and weak bonding between molecular oxygen and graphene zigzag edges at low temperatures

Electron paramagnetic resonance (EPR) study of air-physisorbed defective carbon nano-onions evidences in favor of microwave assisted formation of weakly-bound paramagnetic complexes comprising negatively-charged O2- ions and edge carbon atoms carrying pi-electronic spins. These complexes being located on the graphene edges are stable at low temperatures but irreversibly dissociate at temperatures above 50-60 K. These EPR findings are justified by density functional theory (DFT) calculations demonstrating transfer of an electron from the zigzag edge of graphene-like material to oxygen molecule physisorbed on the graphene sheet edge. This charge transfer causes changing the spin state of the adsorbed oxygen molecule from S = 1 to S = 1/2 one. DFT calculations show significant changes of adsorption energy of oxygen molecule and robustness of the charge transfer to variations of the graphene-like substrate morphology (flat and corrugated mono- and bi-layered graphene) as well as edges passivation. The presence of H- and COOH- terminated edge carbon sites with such corrugated substrate morphology allows formation of ZE-O2- paramagnetic complexes characterized by small (<50 meV) binding energies and also explains their irreversible dissociation as revealed by EPR.

cond-mat.mes-hall↗