arXiv2015

Nanoindentation of Porous Bulk and Thin Films of LSCF

In this paper we show how reliable measurements on porous ceramic films can be made by appropriate nanoindentation experiments and analysis. Room-temperature mechanical properties of the mixed-conducting perovskite material LSCF6428 were investigated by nanoindentation of porous bulk samples and porous films sintered at temperatures from 900-1200C. A spherical indenter was used so that the contact area was much greater than the scale of the porous microstructure. The elastic modulus of the bulk samples was found to increase from 33.8-174.3 GPa and hardness from 0.64-5.32 GPa as the porosity decreased from 45-5% after sintering at 900-1200C. Densification under the indenter was found to have little influence on the measured elastic modulus. The residual porosity in the dense sample was found to account for the discrepancy between the elastic moduli measured by indentation and by impulse excitation. Crack-free LSCF6428 films of acceptable surface roughness for indentation were also prepared by sintering at 900-1200C. Reliable measurements of the true properties of the films were obtained by data extrapolation provided that the ratio of indentation depth to film thickness was in the range 0.1 to 0.2. The elastic moduli of the films and bulk materials were approximately equal for a given porosity. The 3D microstructures of films before and after indentation were characterized using FIB-SEM tomography. Finite element modelling of the elastic deformation of the actual microstructures showed excellent agreement with the nanoindentation results.

cond-mat.mtrl-sci↗

arXiv2015

Surface quality improvement of porous thin films suitable for nanoindentation

The reliability of perovskite material LSCF to be used as cathode parts in solid oxide fuel cells also relies on its mechanical properties. Adequate surface conditions are desired when the as-sintered porous thin films are subjected to nanoindentation for mechanical property determination. In this study, extensive cracks and considerable surface roughness were found in the LSCF films after sintering at high temperatures. This would significantly scatter the nanoindentation data and result in unreliable measurements. Various attempts including the comparison of film deposition methods, drying and sintering processes, and reformulating the ink were made to improve the surface quality. Results revealed little dependence of cracking and surface roughness on deposition methods, drying or sintering processes. It was found that the critical factor for obtaining crack-free and smooth LSCF films was the ability of the ink to be self-levelling in the earlier wet state. Reproducible nanoindentation measurements were obtained for the films with improved surface quality.

cond-mat.mtrl-sci↗

arXiv2015

Analyses of microstructural and elastic properties of porous SOFC cathodes based on focused ion beam tomography

Mechanical properties of porous SOFC electrodes are largely determined by their microstructures. Measurements of the elastic properties and microstructural parameters can be achieved by modelling of the digitally reconstructed 3D volumes based on the real electrode microstructures. However, the reliability of such measurements is greatly dependent on the processing of raw images acquired for reconstruction. In this work, the actual microstructures of La0.6Sr0.4Co0.2Fe0.8O3-d (LSCF) cathodes sintered at an elevated temperature were reconstructed based on dual-beam FIB/SEM tomography. Key microstructural and elastic parameters were estimated and correlated. Analyses of their sensitivity to the grayscale threshold value applied in the image segmentation were performed. The important microstructural parameters included porosity, tortuosity, specific surface area, particle and pore size distributions, and inter-particle neck size distribution, which may have varying extent of effect on the elastic properties simulated from the microstructures using FEM. Results showed that different threshold value range would result in different degree of sensitivity for a specific parameter. The estimated porosity and tortuosity were more sensitive than surface area to volume ratio. Pore and neck size were found to be less sensitive than particle size. Results also showed that the modulus was essentially sensitive to the porosity which was largely controlled by the threshold value.

cond-mat.mtrl-sci↗