SearcharxivSearch

arXiv subjects

Hyeonoh Jo

Publications and source records attributed to Hyeonoh Jo.

2 recordsLinked to original sources

GaN Nucleation Landscape on Patterned Sapphire Shaped by the Growth Temperature of Directly Grown Boron-Compound Masks

The growth temperature of directly grown boron-compound masks on patterned sapphire can modify the local accessibility of the underlying sapphire surface and thereby alter the subsequent nucleation behavior of GaN. In this work, we investigate how ammonia-borane-derived boron-compound masks grown at different temperatures shape the GaN nucleation landscape within circular SiO$_2$ openings during the initial stage of epitaxial lateral overgrowth. The preferential nucleation position of GaN changes systematically with mask growth temperature: masks grown at 700--750$^\circ$C produce pronounced edge-biased distributions, whereas higher-temperature masks lead to more inward-shifted and spatially sparse GaN domains. Quantitative analysis of the GaN areal fraction, the number of visibly isolated domains, and the radial distribution of domain centers shows that the mask growth temperature affects both the amount of GaN coverage and the spatial arrangement of GaN domains within each opening. The nonmonotonic change in the number of visibly isolated domains is interpreted as a consequence of competition between reduced lateral merging and reduced effective substrate accessibility, rather than as a direct measure of the number of active nucleation sites. Kinetic Monte Carlo simulations reproduce the essential experimental trends by varying the effective density and radial distribution of substrate-accessible sites. These results suggest that the growth temperature of directly formed boron-compound masks provides a practical means of reshaping the intra-opening GaN nucleation landscape by controlling the spatial distribution and effectiveness of local pathways through which GaN precursors can access the underlying sapphire surface.

cond-mat.mtrl-sci

Orientation disparity in GaN/graphene/$m$-sapphire: control-based re-examination of thru-hole epitaxy

The crystallographic orientation of films grown on 2D-masked substrates is often used to infer the pathway among remote, van der Waals, and thru-hole (pinhole-seeded) epitaxy. However, attribution of a specific growth mechanism based on orientation can be ambiguous unless mask continuity and substrate pre-treatment are evaluated within a single process window. We compare GaN grown under identical conditions on four m-plane sapphire templates: (i) bare, (ii) "graphene-grown" (high-temperature Ar/H2 with CH4 on), (iii) "anneal-only" (high-temperature Ar/H2 with CH4 off), and (iv) graphene oxide spin-coated and reduced on pristine sapphire. GaN selects (103) on graphene-grown and anneal-only m-plane sapphire, selects (100) on bare m-plane sapphire, and is predominantly (100) with a minority (103) on graphene oxide spin-coated and reduced/pristine m-plane sapphire. High-resolution TEM shows that, on partly graphene-covered samples, nucleation occurs on exposed sapphire (thru-hole), not on graphene, providing mechanism evidence independent of orientation. Within this window, the substrate surface state set by high-temperature Ar/H2 pre-treatment (rather than mask continuity) primarily governs orientation, while open-area effects can play a secondary role. Thus, preferred orientation alone may not determine the growth mechanism; mask continuity and substrate pre-treatment must be explicitly controlled when using orientation as evidence for mechanism assignment.

cond-mat.mtrl-sci