arXiv2005

Intrinsic and Extrinsic Contributions to the Lattice Parameter of GaMnAs

We report on measurements of the crystal structure and hole density in a series of as-grown and annealed GaMnAs samples. The measured hole densities are used to obtain the fraction of incorporated Mn atoms occupying interstitial and substitutional sites. This allows us to make a direct comparison of the measured lattice parameters with recent density functional theory (DFT) predictions. We find that the decrease in lattice constant observed on annealing is smaller than that predicted due to the out diffusion of interstitial Mn during annealing. The measured lattice parameters after annealing are still significantly larger than that of GaAs even in samples with very low compensation. This indicates that the intrinsic lattice parameter of GaMnAs is significantly larger than that of GaAs, in contradiction to the DFT prediction.

cond-mat.mtrl-sci↗

arXiv2004

Magnetism in (Ga,Mn)As Thin Films With TC Up To 173K

We have investigated the magnetic properties of (Ga,Mn)As thin films with Mn concentration between 1 and 9%. Ferromagnetic transition temperatures TC of up to 173K are observed. The results are compared to the predictions of the Zener mean-field theory. We find no evidence of a fundamental limit to TC.

cond-mat.str-el↗

arXiv2004

Search For Hole Mediated Ferromagnetism In Cubic (Ga,Mn)N

Results of magnetisation measurements on p-type zincblende-(Ga,Mn)N are reported. In addition to a small high temperature ferromagnetic signal, we detect ferromagnetic correlation among the remaining Mn ions, which we assign to the onset of hole-mediated ferromagnetism in (Ga,Mn)N.

cond-mat.mtrl-sci↗

arXiv2004

In-plane uniaxial anisotropy rotations in (Ga,Mn)As thin films

We show, by SQUID magnetometry, that in (Ga,Mn)As films the in-plane uniaxial magnetic easy axis is consistently associated with particular crystallographic directions and that it can be rotated from the [-110] direction to the [110] direction by low temperature annealing. We show that this behavior is hole-density-dependent and does not originate from surface anisotropy. The presence of uniaxial anisotropy as well its dependence on the hole-concentration and temperature can be explained in terms of the p-d Zener model of the ferromagnetism assuming a small trigonal distortion.

cond-mat.mtrl-sci↗

arXiv2004

Large tunneling anisotropic magnetoresistance in (Ga,Mn)As nanoconstrictions

We report a large tunneling anisotropic magnetoresistance (TAMR) in a thin (Ga,Mn)As epilayer with lateral nanoconstrictions. The observation establishes the generic nature of this effect, which originates from the spin-orbit coupling in a ferromagnet and is not specific to a particular tunnel device design. The lateral geometry allows us to link directly normal anisotropic magnetoresistance (AMR) and TAMR. This indicates that TAMR may be observable in other materials showing a comparable AMR at room temperature, such as transition metal alloys.

cond-mat.mes-hall↗

arXiv2003

P-type conductivity in cubic GaMnN layers grown by molecular beam epitaxy

Cubic (zinc-blende) Ga1-xMnxN layers were grown by plasma-assisted molecular beam epitaxy on GaAs (001) substrates. Some of the structures also contained cubic AlN buffer layers. Auger Electron Spectroscopy and Secondary Ion Mass Spectroscopy studies clearly confirmed the incorporation of Mn into cubic GaN, the Mn being uniformly distributed through the layer. X-ray diffraction studies demonstrated that the Mn-doped GaN films are cubic and do not show phase separation up to a Mn concentrations of x<0.1. P-type conductivity for the cubic Ga1-xMnxN layers was observed for a wide range of the Mn doping levels. The measured hole concentration at room temperature depends non-linearly on the Mn incorporation and varies from 3x10^16 to 5x10^18 cm-3.

cond-mat.mtrl-sci↗

arXiv2003

New Sol-Gel Synthesis of Ordered Nanostructured Doped ZnO Films

A novel sol-gel route to c-axis orientated undoped and Co, Fe, Mn and V doped ZnO films is reported. Sols were prepared from a hydrated zinc acetate precursor and dimethyl formamide (DMF) solvent. Films were spin-coated on to hydrophilic sapphire substrates then dried, annealed and post-annealed, producing almost purely uniaxial ZnO crystallites and a high degree of long-range structural order. Specific orientation of hexagonal crystallites is demonstrated both perpendicular and parallel to the substrate surface. Cobalt doping resulted in the formation of columnar ZnO nanocrystals. Vanadium doped films formed the spinel oxide ZnAl2O4, resulting from the reaction between ZnO and the sapphire substrate. Structural, optical and morphological characterisation demonstrated the high quality of the films.

cond-mat.mtrl-sci↗

arXiv2003

Mn Interstitial Diffusion in (Ga,Mn)As

We present a combined theoretical and experimental study of the ferromagnetic semiconductor (Ga,Mn)As which explains the remarkably large changes observed on low temperature annealing. Careful control of the annealing conditions allows us to obtain samples with ferromagnetic transition temperatures up to 159 K. Ab initio calculations, and resistivity measurements during annealing, show that the observed changes are due to out-diffusion of Mn interstitials towards the surface, governed by an energy barrier of about 0.7-0.8 eV. The Mn interstitial is a double donor resulting in compensation of charge carriers and suppression of ferromagnetism. Electric fields induced by high concentrations of substitutional Mn acceptors have a significant effect on the diffusion.

cond-mat.mtrl-sci↗

arXiv2003

DC-transport properties of ferromagnetic (Ga,Mn)As semiconductors

We study the dc transport properties of (Ga,Mn)As diluted magnetic semiconductors with Mn concentration varying from 1.5% to 8%. Both diagonal and Hall components of the conductivity tensor are strongly sensitive to the magnetic state of these semiconductors. Transport data obtained at low temperatures are discussed theoretically within a model of band-hole quasiparticles with a finite spectral width due to elastic scattering from Mn and compensating defects. The theoretical results are in good agreement with measured anomalous Hall effect and anisotropic longitudinal magnetoresistance data. This quantitative understanding of dc magneto-transport effects in (Ga,Mn)As is unparalleled in itinerant ferromagnetic systems.

cond-mat.mtrl-sci↗

arXiv2002

Anisotropic Magnetoresistance in GaMnAs films

The magnetoresistance in a series of Ga1-xMnxAs samples with 0.2 =< x =< 0.8 have been measured for three mutually orthogonal orientations of the external magnetic field. The anisotropy magnetoresistance decreases with increasing of the Mn content, which means that the magnetic disorder or defects scattering increases with increasing of Mn content. And also the magneto-crystalline anisotropy increases with increasing of Mn concentration.

cond-mat.mtrl-sci↗

arXiv2002

High Curie temperature GaMnAs obtained by resistance-monitored annealing

We show that by annealing Ga1-xMnxAs thin films at temperatures significantly lower than in previous studies, and monitoring the resistivity during growth, an unprecedented high Curie temperature Tc and conductivity can be obtained. Tc is unambiguously determined to be 118 K for Mn concentration x=0.05, 140 K for x=0.06, and 120 K for x=0.08. We also identify a clear correlation between Tc and the room temperature conductivity. The results indicate that Curie temperatures significantly in excess of the current values are achievable with improvements in growth and post-growth annealing conditions.

cond-mat.mtrl-sci↗

arXiv2002

The Hall effect and hole densities in high Tc GaMnAs thin films

By studying the Hall effect in a series of low resistivity Ga1-xMnxAs samples, accurate values for the hole density p, Mn concentration x, and Curie temperature Tc are obtained over the range 0.015=<x=<0.08. The hole density corresponds to 90% of the Mn concentration at low x, and has a maximum value of 1.0x10-27 m-3 when Tc=125K for x=0.06. This data allows the first meaningful comparison of mean field predicted Curie temperatures with experiment over a wide range of x. The theory is in qualitative agreement with experiment, but overestimates Tc at large x and underestimates TC at low x.

cond-mat.mtrl-sci↗