Publications and source records attributed to L. Ley.
We report on the observation of inertial-ballistic transport in nanoscale cross junctions fabricated from epitaxial graphene grown on SiC(0001). Ballistic transport is indicated by a negative bend resistance of R12,43 ~ 170 ohm which is measured in a non-local, four-terminal configuration at 4.2 K and which vanishes as the temperature is increased above 80 K.
We have studied the electronic structure of the interface between 6H-SiC{0001} and graphite. On n-type and p-type 6H-SiC(0001) we observe Schottky barriers of Phi_b,n^Si= 0.3+-0.1eV and Phi_b,p^Si=2.7+-0.1eV, respectively. The observed barrier is face specific: on n-type 6H-SiC(000-1) we find Phi_b,n^C=1.3+-0.1eV. The impact of these barriers on the electrical properties of metal/SiC contacts is discussed.
Graphitization of the 6H-SiC(0001) surface as a function of annealing temperature has been studied by ARPES, high resolution XPS, and LEED. For the initial stage of graphitization - the 6root3 reconstructed surface - we observe sigma-bands characteristic of graphitic sp2-bonded carbon. The pi-bands are modified by the interaction with the substrate. C1s core level spectra indicate that this layer consists of two inequivalent types of carbon atoms. The next layer of graphite (graphene) formed on top of the 6root3 surface at TA=1250-1300 degree C has an unperturbed electronic structure. The annealing at higher temperatures results in the formation of a multilayer graphite film. It is shown that the atomic arrangement of the interface between graphite and the SiC(0001) surface is practically identical to that of the 6root3 reconstructed layer.