arXiv2025

Oriented 2D Ruddlesden-Popper Metal Halides by Pulsed Laser Deposition

Two-dimensional (2D) Ruddlesden-Popper (RP) Metal Halides present unique and tunable properties. However, direct and oriented synthesis is challenging due to low formation energies that lead to rapid, uncontrolled growth during solution-based processing. Here, we report the solvent-free growth of oriented and n = 1 2D $(\mbox{PEA})_2\mbox{PbI}_4$ RP films by pulsed laser deposition (PLD). In situ photoluminescence (PL) during deposition reveals formation of the n =1 phase at the ear;y stages of growth. X-ray diffraction (XRD) and grazing-incidence wide-angle scattering (GIWAXS) confirm a single oriented n = 1 phase, independent of the substrate. Co-localized spatially resolved PL and AFM further validate the conformal growth on strained epitaxial $\mbox{MAPbI}_3$ remain stable for over 184 days without any sign of cation exchange. This work highlights the potential of PLD for direct, room-temperature synthesis of 2D $(\mbox{PEA})_2\mbox{PbI}_4$ RP films and stable 2D/3D heterostructures.

cond-mat.mtrl-sci↗

arXiv2024

From design to device: challenges and opportunities in computational discovery of p-type transparent conductors

A high-performance p-type transparent conductor (TC) does not yet exist, but could lead to advances in a wide range of optoelectronic applications and enable new architectures for, e.g., next-generation photovoltaic (PV) devices. High-throughput computational material screenings have been a promising approach to filter databases and identify new p-type TC candidates, and some of these predictions have been experimentally validated. However, most of these predicted candidates do not have experimentally-achieved properties on par with n-type TCs used in solar cells, and therefore have not yet been used in commercial devices. Thus, there is still a significant divide between transforming predictions into results that are actually achievable in the lab, and an even greater lag in scaling predicted materials into functional devices. In this perspective, we outline some of the major disconnects in this materials discovery process -- from scaling computational predictions into synthesizable crystals and thin films in the laboratory, to scaling lab-grown films into real-world solar devices -- and share insights to inform future strategies for TC discovery and design.

physics.app-ph↗

arXiv2024

Charge Transport and Defects in Sulfur-Deficient Chalcogenide Perovskite BaZrS$_3$

Exploring the conduction mechanism in the chalcogenide perovskite BaZrS$_3$ is of significant interest due to its potential suitability as a top absorber layer in silicon-based tandem solar cells and other optoelectronic applications. Theoretical and experimental studies anticipate native ambipolar doping in BaZrS$_3$, although experimental validation remains limited. This study reveals a transition from highly insulating behavior to n-type conductivity in BaZrS$_3$ through annealing in an S-poor environment. BaZrS$_3$ thin films are synthesized $\textit{via}$ a two step process: co-sputtering of Ba-Zr followed by sulfurization at 600 $^{\circ}$C, and subsequent annealing in high vacuum. UV-Vis measurement reveal a red-shift in the absorption edge concurrent with sample color darkening after annealing. The increase in defect density with vacuum annealing, coupled with low activation energy and n-type character of defects, strongly suggests that sulfur vacancies (V$_{\mathrm{S}}$) are responsible, in agreement with theoretical predictions. The shift of the Fermi level towards conduction band minimum, quantified by Hard X-ray Photoelectron Spectroscopy (Ga K$α$, 9.25 keV), further corroborates the induced n-type of conductivity in annealed samples. Our findings indicate that vacuum annealing induces V$_{\mathrm{S}}$ defects that dominate the charge transport, thereby making BaZrS$_3$ an n-type semiconductor under S-poor conditions. This study offers crucial insights into understanding the defect properties of BaZrS$_3$, facilitating further improvements for its use in solar cell applications.

cond-mat.mtrl-sci↗

arXiv2023

Impact of TCO Microstructure on the Electronic Properties of Carbazole-based Self-Assembled Monolayers

Carbazole-based self-assembled monolayers (PACz-SAMs), anchored via their phosphonic acid group on a transparent conductive oxide (TCO) have demonstrated excellent performance as hole-selective layers in inverted perovskite solar cells. However, the influence of the TCO microstructure on the work function (WF) shift after SAM anchoring as well as the WF variations at the micro/nanoscale have not been extensively studied yet. Herein, we investigate the effect of the Sn-doped In2O3 (ITO) microstructure on the WF distribution upon 2PACz-SAMs and NiOx/2PACz-SAMs application. For this, ITO substrates with amorphous and polycrystalline (featuring either nanoscale or microscale-sized grains) microstructures are studied. A correlation between the ITO grain orientation and 2PACz-SAMs local potential distribution was found via Kelvin probe force microscopy and electron backscatter diffraction. These variations vanish for amorphous ITO or when adding an amorphous NiOx buffer layer, where a homogeneous surface potential distribution is mapped. Ultraviolet photoelectron spectroscopy confirmed the ITO WF increase after 2PACz-SAMs deposition. Considering the importance of polycrystalline TCOs as high mobility and broadband transparent electrodes, we provide insights to ensure uniform WF distribution upon application of hole transport SAMs, which is critical towards enhanced device performance.

cond-mat.mtrl-sci↗

arXiv2020

Single-source, solvent-free, room temperature deposition of black $γ$-CsSnI$_3$ films

The presence of a non-optically active polymorph (yellow-phase) competing with the optically active polymorph (black $γ$-phase) at room temperature in CsSnI3 and the susceptibility of Sn to oxidation, represent two of the biggest obstacles for the exploitation of CsSnI3 in optoelectronic devices. Here room-temperature single-source in vacuum deposition of smooth black $γ$ - CsSnI3 thin films is reported. This has been done by fabricating a solid target by completely solvent-free mixing of CsI and SnI2 powders and isostatic pressing. By controlled laser ablation of the solid target on an arbitrary substrate at room temperature, the formation of CsSnI3 thin films with optimal optical properties is demonstrated. The films present a band gap of 1.32 eV, a sharp absorption edge and near-infrared photoluminescence emission. These properties and X-ray diffraction of the thin films confirmed the formation of the orthorhombic (B-$γ$) perovskite phase. The thermal stability of the phase was ensured by applying in situ an Al2O$_3$ capping layer. This work demonstrates the potential of pulsed laser deposition as a volatility-insensitive single-source growth technique of halide perovskites and represents a critical step forward in the development and future scalability of inorganic lead-free halide perovskites.

physics.app-ph↗

arXiv2019

Exploring co-sputtering of ZnO:Al and SiO2 for efficient electron-selective contacts on silicon solar cells

In recent years, considerable efforts have been devoted to developing novel electron-selective materials for crystalline Si (c-Si) solar cells with the attempts to simplify the fabrication process and improve efficiency. In this study, ZnO:Al (AZO) is co-sputtered with SiO2 to form AZO:SiO2 films with different SiO2 content. These nanometer-scale films, deposited on top of thin intrinsic hydrogenated amorphous silicon films and capped with low-work-function metal (such as Al and Mg), are demonstrated to function effectively as electron-selective contacts in c-Si solar cells. On the one hand, AZO:SiO2 plays an important role in such electron-selective contact and its thickness is a critical parameter, thickness of 2 nm showing the best. On the other hand, at the optimal thickness of AZO:SiO2, the open circuit voltage (VOC) of the solar cells is found to be relatively insensitive to either the work function or the band gap of AZO:SiO2. Whereas, regarding the fill factor (FF), AZO without SiO2 content exhibits to be the optimal choice. By using AZO/Al as electron-selective contact, we successfully realize a 19.5%-efficient solar cell with VOC over 700 mV and FF around 75%, which is the best result among c-Si solar cells using ZnO as electron-selective contact. Also, this work implies that efficient carrier-selective film can be made by magnetron sputtering method.

physics.app-ph↗

arXiv2013

Copper and Transparent-Conductor Reflectarray Elements on Thin-Film Solar Cell Panels

This work addresses the integration of reflectarray antennas (RA) on thin film Solar Cell (SC) panels, as a mean to save real estate, weight, or cost in platforms such as satellites or transportable autonomous antenna systems. Our goal is to design a good RA unit cell in terms of phase response and bandwidth, while simultaneously achieving high optical transparency and low microwave loss, to preserve good SC and RA energy efficiencies, respectively. Since there is a trade-off between the optical transparency and microwave surface conductivity of a conductor, here both standard copper and transparent conductors are considered. The results obtained at the unit cell level demonstrates the feasibility of integrating RA on a thin-film SC, preserving for the first time good performance in terms of both SC and RA efficiency. For instance, measurement at X-band demonstrate families of cells providing a phase range larger than 270° with average microwave loss of -2.45dB (resp. -0.25dB) and average optical transparency in the visible spectrum of 90% (resp. 85%) using transparent conductive multilayer (resp. a copper layer).

physics.optics↗

arXiv2010

Towards a Quantitative Description of Solid Electrolyte Conductance Switches

We present a quantitative analysis of the steady state electronic transport in a resistive switching device. The device is composed of a thin film of Ag$_{2}$S (solid electrolyte) contacted by a Pt nano-contact acting as ion-blocking electrode, and a large area Ag reference electrode. When applying a bias voltage both ionic and electronic transport occurs, and depending on the polarity it causes an accumulation of ions around the nano-contact. At small applied voltages (pre-switching) we observed this as a strongly nonlinear current-voltage curve, which have been modeled using the Hebb-Wagner treatment for polarization of a mixed conductor. This model correctly describes the transport of the electrons within the polarized solid electrolyte in the steady state up until the resistance switching, covering the entire range of non-stoichiometries, and including the supersaturation range just before the deposition of elemental silver. In this way, it is a step towards a quantitative understanding of the processes that lead to resistance switching.

cond-mat.mtrl-sci↗