S. E. Lofland

Publications and source records attributed to S. E. Lofland.

7 recordsLinked to original sources
arXiv2005

Large Second Harmonic Kerr rotation in GaFeO3 thin films on YSZ buffered Silicon

Epitaxial thin films of gallium iron oxide (GaFeO3) are grown on (001) silicon by pulsed laser deposition (PLD) using yttrium-stabilized zirconia (YSZ) buffer layer. The crystalline template buffer layer is in-situ PLD grown through the step of high temperature stripping of the intrinsic silicon surface oxide. The X-ray diffraction pattern shows c-axis orientation of YSZ and b-axis orientation of GaFeO3 on Si (100) substrate. The ferromagnetic transition temperature (TC ~ 215 K) is in good agreement with the bulk data. The films show a large nonlinear second harmonic Kerr rotation of ~15 degrees in the ferromagnetic state.

cond-mat.mtrl-sci↗
arXiv2003

Co-doped LaLa1-xSrxTiO3-d : A Diluted Magnetic Oxide System with High Curie Temperature

Ferromagnetism is observed at and above room temperature in pulsed laser deposited epitaxial films of Co-doped Ti-based oxide perovskite (La1-xSrxTiO3-d). The system has the characteristics of an intrinsic diluted magnetic semiconductor (metal) at low concentrations (<~ 2 %), but develops inhomogeneity at higher cobalt concentrations. The films range from being opaque metallic to transparent semiconducting depending on the oxygen pressure during growth and are yet ferromagnetic.

cond-mat.str-el↗
arXiv2003

Temperature Dependence of Microwave Loss, Electronic Transport and Magnetic Parameters in Polycrystalline Perovskite Manganites - Evidence that the Magnetic and the Metal-Insulator Transitions are not Identical

Measurements of the variation with temperature of the dc resistivity, ac susceptibility, dc magnetization and microwave loss for several systems of pseudo-cubic manganites reveal that the characteristic temperatures delineated by the various properties can be very The observations further suggest that both the transitions are percolative in nature and therefore there is no a priori reason for them to be identical.

cond-mat↗
arXiv2003

High Temperature Ferromagnetism with Giant Magnetic Moment in Transparent Co-doped SnO2-d

Occurrence of room temperature ferromagnetism is demonstrated in pulsed laser deposited thin films of Sn1-xCoxO2-d (x<0.3). Interestingly, films of Sn0.95Co0.05O2-d grown on R-plane sapphire not only exhibit ferromagnetism with a Curie temperature close to 650 K, but also a giant magnetic moment of about 7 Bohr-Magneton/Co, not yet reported in any diluted magnetic semiconductor system. The films are semiconducting and optically highly transparent.

cond-mat↗
arXiv2002

Ferromagnetism in laser deposited anatase Ti$_{1-x}$Co$_{x}$O$_{2-$δ$}$ films

Pulsed laser deposited films of Co doped anatase TiO2 are examined for Co substitutionality, ferromagnetism, transport, magnetotransport and optical properties. Our results show limited solubility (up to ~ 2 %) of Co in the as-grown films and formation of Co clusters thereafter. For Ti0.93Co0.07O2-d sample, which exhibits a Curie temperature (Tc) over 1180 K, we find the presence of 20-50 nm Co clusters as well as a small concentration of Co incorporated into the remaining matrix. After being subjected to the high temperature anneal during the first magnetization measurement, the very same sample shows a Tc ~ 650 K and almost full matrix incorporation of Co. This Tc is close to that of as-grown Ti0.99Co0.01O2-d sample (~ 700 K). The transport, magnetotransport and optical studies also reveal interesting effects of the matrix incorporation of Co. These results are indicative of an intrinsic Ti1-xCoxO2-d diluted magnetic semiconductor with Tc of about 650-700 K.

cond-mat↗