Nanogranular MgB2 thin films on SiC buffered Si substrates prepared by in-situ method

MgB2 thin films were deposited on SiC buffered Si substrates by sequential electron beam evaporation of B-Mg bilayer followed by in-situ annealing. The application of a SiC buffer layer enables the maximum annealing temperature of 830 C. The Transmission Electron Microscopy analysis confirms the growth of a nanogranular MgB2 film and the presence of a Mg2Si compound at the surface of the film. The 150-200 nm thick films show a maximum zero resistance critical temperature TC0 above 37 K and a critical current density JC ~ 106 A/cm2 at 11K.

cond-mat.supr-con↗

arXiv2004

Electrical and structural properties of MgB2 films prepared by sequential deposition of B and Mg on the NbN buffered Si(100) substrate

We introduce a simple method of an MgB2 film preparation using sequential electron-beam evaporation of B-Mg two-layer (followed by in-situ annealing) on the NbN buffered Si(100) substrate. The Transmission Electron Microscopy analyses confirm a growth of homogeneous nanogranular MgB2 films without the presence of crystalline MgO. A sensitive measurement of temperature dependence of microwave losses shows a presence of intergranular weak links close the superconducting transition only. The MgB2 films obtained, about 200 nm thick, exhibit a maximum zero resistance critical temperature of 36 K and critical current density of 3x10^7 A/cm^2 at 13.2 K

cond-mat.supr-con↗