arXiv2006

Enhanced critical current density of MgB2 superconductor synthesized in high magnetic fields

The effect of high magnetic fields on the current carrying properties of both MgB2 bulks and Fe-sheathed tapes was investigated following different thermal sequences. It is found that application of a large magnetic field during processing results in the quite uniform microstructure and the better connectivity between the MgB2 grains. As a result, the Jc of these samples has shown much higher value than that of the MgB2 samples in the absence of magnetic field. The possible mechanism of the Jc enhancement under an external magnetic field is also discussed.

cond-mat.supr-con↗

arXiv2006

Enhancement of JC-B Properties in MoSi2 doped MgB2 tapes

MoSi2 doped MgB2 tapes with different doping levels were prepared through the in-situ powder-in-tube method using Fe as the sheath material. Effect of MoSi2 doping on the MgB2/Fe tapes was investigated. It is found that the highest JC value was achieved in the 2.5 at.% doped samples, more than a factor of 4 higher compared to the undoped tapes at 4.2 K, 10 T, then further increasing the doping ratio caused a reduction of JC. Moreover, all doped tapes exhibited improved magnetic field dependence of Jc. The enhancement of JC-B properties in MoSi2 doped MgB2 tapes is attributed to good grain linkage and the introduction of effective flux pining centers with the doping.

cond-mat.supr-con↗

arXiv2006

Significantly enhanced critical current densities in MgB2 tapes made by a scaleable, nano-carbon addition route

Nanocarbon-doped Fe-sheathed MgB2 tapes with different doping levels were prepared by the in situ powder-in-tube method. Compared to the undoped tapes, Jc for all the C-doped samples was enhanced by more than an order of magnitude in magnetic fields above 9 T. At 4.2 K, the transport Jc for the 5 at% doped tapes reached 1.85x104 A/cm2 at 10 T and 2.8x103 A/cm2 at 14 T, respectively. Moreover, the critical temperature for the doped tapes decreased slightly. Transmission electron microscopy showed a number of intra-granular dislocations and the dispersed nanoparticles embedded within MgB2 grains induced by the C doping. The mechanism for the enhancement of flux pinning is also discussed. These results indicate that powder-in-tube-processed MgB2 tape is very promising for high-field applications.

cond-mat.supr-con↗

arXiv2005

Effect of nano-C doping on the in-situ processed MgB2 tapes

The effect of nano-C doping on the microstructure and superconducting properties of Fe-sheathed MgB2 tapes prepared through the in-situ powder-in-tube method was studied. Heat treatment was performed at a low temperature of 650C for 1 h. Scanning electron microscopy investigation revealed that the smaller grain size of MgB2 in the samples with the C-doping. Further, the a-axis lattice parameter and transition temperature decreased monotonically with increasing doping level, which is due to the C substitution for B. High critical current density Jc values in magnetic fields were achieved in the doped samples because of the very fine-grained microstructure of the superconducting phase obtained with C doping.

cond-mat.supr-con↗