arXiv2021

Low-density superconductivity in SrTiO$_3$ bounded by the adiabatic criterion

SrTiO$_3$ exhibits superconductivity for carrier densities $10^{19}-10^{21}$ cm$^{-3}$. Across this range, the Fermi level traverses a number of vibrational modes in the system, making it ideal for studying dilute superconductivity. We use high-resolution planar-tunneling spectroscopy to probe chemically-doped SrTiO$_3$ across the superconducting dome. The over-doped superconducting boundary aligns, with surprising precision, to the Fermi energy crossing the Debye energy. Superconductivity emerges with decreasing density, maintaining throughout the Bardeen-Cooper-Schrieffer (BCS) gap to transition-temperature ratio, despite being in the anti-adiabatic regime. At lowest superconducting densities, the lone remaining adiabatic phonon van Hove singularity is the soft transverse-optic mode, associated with the ferroelectric instability. We suggest a scenario for pairing mediated by this mode in the presence of spin-orbit coupling, which naturally accounts for the superconducting dome and BCS ratio.

cond-mat.supr-con↗

arXiv2021

Universal behavior of the bosonic metallic ground state in a two-dimensional superconductor

Anomalous metallic behavior, marked by a saturating finite resistivity much lower than the Drude estimate, has been observed in a wide range of two-dimensional superconductors. Utilizing the electrostatically gated LaAlO3/SrTiO3 interface as a versatile platform for superconductor-metal quantum phase transitions, we probe variations in the gate, magnetic field, and temperature to construct a phase diagram crossing from superconductor, anomalous metal, vortex liquid, to Drude metal states, combining longitudinal and Hall resistivity measurements. We find that the anomalous metal phases induced by gating and magnetic field, although differing in symmetry, are connected in the phase diagram and exhibit similar magnetic field response approaching zero temperature. Namely, within a finite regime of the anomalous metal state, the longitudinal resistivity linearly depends on field while the Hall resistivity diminishes, indicating an emergent particle-hole symmetry. The universal behavior highlights the uniqueness of the quantum bosonic metallic state, distinct from bosonic insulators and vortex liquids.

cond-mat.supr-con↗

arXiv2020

Charge order textures induced by non-linear lattice coupling in a half-doped manganite

The self-organization of strongly interacting electrons into superlattice structures underlies the properties of many quantum materials. How these electrons arrange within the superlattice dictates what symmetries are broken and what ground states are stabilized. Here we show that cryogenic scanning transmission electron microscopy enables direct mapping of local symmetries and order at the intra-unit-cell level in the model charge-ordered system Nd$_{1/2}$Sr$_{1/2}$MnO$_{3}$. In addition to imaging the prototypical site-centered charge order, we discover the nanoscale coexistence of an exotic intermediate state which mixes site and bond order and breaks inversion symmetry. We further show that nonlinear coupling of distinct lattice modes controls the selection between competing ground states. The results demonstrate the importance of lattice coupling for understanding and manipulating the character of electronic self-organization and highlight a novel method for probing local order in a broad range of strongly correlated systems.

cond-mat.str-el↗

arXiv2020

Giant strain gradient elasticity in SrTiO3 membranes: bending versus stretching

Young's modulus determines the mechanical loads required to elastically stretch a material, and also, the loads required to bend it, given that bending stretches one surface while compressing the opposite one. Flexoelectric materials have the additional property of becoming electrically polarized when bent. While numerous studies have characterized this flexoelectric coupling, its impact on the mechanical response, due to the energy cost of polarization upon bending, is largely unexplored. This intriguing contribution of strain gradient elasticity is expected to become visible at small length scales where strain gradients are geometrically enhanced, especially in high permittivity insulators. Here we present nano-mechanical measurements of freely suspended SrTiO3 membrane drumheads. We observe a striking non-monotonic thickness dependence of Young's modulus upon small deflections. Furthermore, the modulus inferred from a predominantly bending deformation is three times larger than that of a predominantly stretching deformation for membranes thinner than 20 nm. In this regime we extract a giant strain gradient elastic coupling of ~2.2e-6 N, which could be used in new operational regimes of nano-electro-mechanics.

cond-mat.mtrl-sci↗

arXiv2018

Dual-Gate Modulation of Carrier Density and Disorder in an Oxide Two-Dimensional Electron System

Carrier density and disorder are two crucial parameters that control the properties of correlated two-dimensional electron systems. In order to disentangle their individual contributions to quantum phenomena, independent tuning of these two parameters is required. Here, by utilizing a hybrid liquid/solid electric dual-gate geometry acting on the conducting LaAlO3/SrTiO3 heterointerface, we obtain an additional degree of freedom to strongly modify the electron confinement profile and thus the strength of interfacial scattering, independent from the carrier density. A dual-gate controlled nonlinear Hall effect is a direct manifestation of this profile, which can be quantitatively understood by a Poisson-Schrodinger subband model. In particular, the large nonlinear dielectric response of SrTiO3 enables a very wide range of tunable density and disorder, far beyond that for conventional semiconductors. Our study provides a broad framework for understanding various reported phenomena at the LaAlO3/SrTiO3 interface.

cond-mat.str-el↗

arXiv2018

The density and disorder tuned superconductor-metal transition in two dimensions

Quantum ground states which arise at atomically controlled oxide interfaces provide an opportunity to address key questions in condensed matter physics, including the nature of two-dimensional (2D) metallic behaviour often observed adjacent to superconductivity. At the superconducting LaAlO3/SrTiO3 interface, a metallic ground state emerges upon the collapse of superconductivity with field-effect gating. Strikingly, such metallicity is accompanied with a pseudogap. Here, we utilize independent control of carrier density and disorder of the interfacial superconductor using dual electrostatic gates, which enables the comprehensive examination of the electronic phase diagram approaching zero temperature. We find that the pseudogap corresponds to precursor pairing, and the onset of long-range phase coherence forms a 2D superconducting dome as a function of the dual gate voltages. The gate-tuned superconductor-metal transitions are driven by macroscopic phase fluctuations of Josephson coupled superconducting puddles.

cond-mat.supr-con↗

arXiv2018

Superconducting tunneling spectroscopy of spin-orbit coupling and orbital depairing in Nb:SrTiO$_3$

We have examined the intrinsic spin-orbit coupling (SOC) and orbital depairing in thin films of Nb-doped SrTiO$_3$ by superconducting tunneling spectroscopy. The orbital depairing is geometrically suppressed in the two-dimensional limit, enabling a quantitative evaluation of the Fermi level spin-orbit scattering using Maki's theory. The response of the superconducting gap under in-plane magnetic fields demonstrates short spin-orbit scattering times $τ_{so} \leq 1.1$ ps. Analysis of the orbital depairing indicates that the heavy electron band contributes significantly to pairing. These results suggest that the intrinsic spin-orbit scattering time in SrTiO$_3$ is comparable to those associated with Rashba effects in SrTiO$_3$ interfacial conducting layers and can be considered significant in all forms of superconductivity in SrTiO$_3$.

cond-mat.supr-con↗

arXiv2018

Imaging and tuning polarity at SrTiO3 domain walls

Electrostatic fields tune the ground state of interfaces between complex oxide materials. Electronic properties, such as conductivity and superconductivity, can be tuned and then used to create and control circuit elements and gate-defined devices. Here we show that naturally occurring twin boundaries, with properties that are different from their surrounding bulk, can tune the LaAlO3/SrTiO3 interface 2DEG at the nanoscale. In particular, SrTiO3 domain boundaries have the unusual distinction of remaining highly mobile down to low temperatures, and were recently suggested to be polar. Here we apply localized pressure to an individual SrTiO3 twin boundary and detect a change in LaAlO3/SrTiO3 interface current distribution. Our data directly confirm the existence of polarity at the twin boundaries, and demonstrate that they can serve as effective tunable gates. As the location of SrTiO3 domain walls can be controlled using external field stimuli, our findings suggest a novel approach to manipulate SrTiO3-based devices on the nanoscale.

cond-mat.mes-hall↗

arXiv2017

Polaronic behavior in a weak coupling superconductor

The nature of superconductivity in the dilute semiconductor SrTiO$_3$ has remained an open question for more than 50 years. The extremely low carrier densities ($10^{18}$ - $10^{20}$ cm$^{-3}$) at which superconductivity occurs suggests an unconventional origin of superconductivity outside of the adiabatic limit on which the Bardeen-Cooper-Schrieffer (BCS) and Migdal-Eliashberg (ME) theories are based. We take advantage of a newly developed method for engineering band alignments at oxide interfaces and access the electronic structure of Nb-doped SrTiO$_3$ using high resolution tunneling spectroscopy. We observe strong coupling to the highest energy longitudinal optic (LO) phonon branch and estimate the doping evolution of the dimensionless electron-phonon interaction strength ($λ$). Upon cooling below the superconducting transition temperature ($T_{\mathrm{c}}$), we observe a single superconducting gap corresponding to the weak-coupling limit of BCS theory, indicating an order of magnitude smaller coupling ($λ_{\textrm{BCS}} \approx 0.1$). These results suggest that despite the strong normal state interaction with electrons, the highest LO phonon does not provide a dominant contribution to pairing. They further demonstrate that SrTiO$_3$ is an ideal system to probe superconductivity over a wide range of carrier density, adiabatic parameter, and electron-phonon coupling strength.

cond-mat.supr-con↗

arXiv2016

Ubiquitous strong electron phonon coupling at the interface of FeSe/SrTiO3

The high temperature superconductivity in single-unit-cell (1UC) FeSe on SrTiO3 (STO)(001) and the observation of replica bands by angle-resolved photoemission spectroscopy (ARPES) have led to the conjecture that the coupling between FeSe electron and the STO phonon is responsible for the enhancement of Tc over other FeSe-based superconductors1,2. However the recent observation of a similar superconducting gap in FeSe grown on the (110) surface of STO raises the question of whether a similar mechanism applies3,4. Here we report the ARPES study of the electronic structure of FeSe grown on STO(110). Similar to the results in FeSe/STO(001), clear replica bands are observed. We also present a comparative study of STO (001) and STO(110) bare surfaces, where photo doping generates metallic surface states. Similar replica bands separating from the main band by approximately the same energy are observed, indicating this coupling is a generic feature of the STO surfaces and interfaces. Our findings suggest that the large superconducting gaps observed in FeSe films grown on two different STO surface terminations are likely enhanced by a common coupling between FeSe electrons and STO phonons.

cond-mat.supr-con↗

arXiv2016

Enhanced Superconducting Transition Temperature due to Tetragonal Domains in Two-Dimensionally Doped SrTiO$_3$

Strontium titanate is a low-temperature, non-Bardeen-Cooper-Schrieffer superconductor that superconducts to carrier concentrations lower than in any other system and exhibits avoided ferroelectricity at low temperatures. Neither the mechanism of superconductivity in strontium titanate nor the importance of the structure and dielectric properties for the superconductivity are well understood. We studied the effects of twin structure on superconductivity in a 5.5-nm-thick layer of niobium-doped SrTiO$_{3}$ embedded in undoped SrTiO$_{3}$. We used a scanning superconducting quantum interference device susceptometer to image the local diamagnetic response of the sample as a function of temperature. We observed regions that exhibited a superconducting transition temperature $T_{c}$ $\gtrsim$ 10% higher than the temperature at which the sample was fully superconducting. The pattern of these regions varied spatially in a manner characteristic of structural twin domains. Our results emphasize that the anisotropic dielectric properties of SrTiO$_{3}$ are important for its superconductivity, and need to be considered in any theory of the mechanism of the superconductivity.

cond-mat.supr-con↗

arXiv2016

Anisotropic transport at the LaAlO3/SrTiO3 interface explained by microscopic imaging of channel-flow over SrTiO3 domains

Oxide interfaces, including the LaAlO3/SrTiO3 interface, have been a subject of intense interest for over a decade due to their rich physics and potential as low dimensional nanoelectronic systems. The field has reached the stage where efforts are invested in developing devices. It is critical now to understand the functionalities and limitations of such devices. Recent scanning probe measurements of the LaAlO3/SrTiO3 interface have revealed locally enhanced current flow and accumulation of charge along channels related to SrTiO3 structural domains. These observations raised a key question regarding the role these modulations play in the macroscopic properties of devices. Here we show that the microscopic picture, mapped by scanning superconducting quantum interference device, accounts for a substantial part of the macroscopically measured transport anisotropy. We compared local flux data with transport values, measured simultaneously, over various SrTiO3 domain configurations. We show a clear relation between maps of local current density over specific domain configurations and the measured anisotropy for the same device. The domains divert the direction of current flow, resulting in a direction dependent resistance. We also show that the modulation can be significant and that in some cases up to 95% of the current is modulated over the channels. The orientation and distribution of the SrTiO3 structural domains change between different cooldowns of the same device or when electric fields are applied, affecting the device behavior. Our results, highlight the importance of substrate physics, and in particular, the role of structural domains, in controlling electronic properties of LaAlO3/SrTiO3 devices. Further, these results point to new research directions, exploiting the STO domains ability to divert or even carry current.

cond-mat.mtrl-sci↗

arXiv2015

Broadband Linear-Dichroic Photodetector in a Black Phosphorus Vertical p-n Junction

The ability to detect light over a broad spectral range is central for practical optoelectronic applications, and has been successfully demonstrated with photodetectors of two-dimensional layered crystals such as graphene and MoS2. However, polarization sensitivity within such a photodetector remains elusive. Here we demonstrate a linear-dichroic broadband photodetector with layered black phosphorus transistors, using the strong intrinsic linear dichroism arising from the in-plane optical anisotropy with respect to the atom-buckled direction, which is polarization sensitive over a broad bandwidth from 400 nm to 3750 nm. Especially, a perpendicular build-in electric field induced by gating in black phosphorus transistors can spatially separate the photo-generated electrons and holes in the channel, effectively reducing their recombination rate, and thus enhancing the efficiency and performance for linear dichroism photodetection. This provides new functionality using anisotropic layered black phosphorus, thereby enabling novel optical and optoelectronic device applications.

cond-mat.mes-hall↗

arXiv2014

Quantum longitudinal and Hall transport at the LaAlO3/SrTiO3 interface at low electron densities

We examined the magneto-transport behavior of electrons confined at the conducting LaAlO3/SrTiO3 interface in the low sheet carrier density regime. We observed well resolved Shubnikov-de Haas quantum oscillations in the longitudinal resistance, and a plateau-like structure in the Hall conductivity. The Landau indices of the plateaus in the Hall conductivity data show spacing close to 4, in units of the quantum of conductance. These experimental features can be explained by a magnetic breakdown transition, which quantitatively explains the area, structure, and degeneracy of the measured Fermi surface.

cond-mat.mtrl-sci↗

arXiv2013

Locally enhanced conductivity due to the tetragonal domain structure in LaAlO$_{3}$/SrTiO$_{3}$ heterointerfaces

The ability to control materials properties through interface engineering is demonstrated by the appearance of conductivity at the interface of certain insulators, most famously the {001} interface of the band insulators LaAlO$_{3}$ and TiO$_{2}$-terminated SrTiO$_{3}$ (STO). Transport and other measurements in this system show a plethora of diverse physical phenomena. To better understand the interface conductivity, we used scanning superconducting quantum interference device microscopy to image the magnetic field locally generated by current in an interface. At low temperature, we found that the current flowed in conductive narrow paths oriented along the crystallographic axes, embedded in a less conductive background. The configuration of these paths changed on thermal cycling above the STO cubic-to-tetragonal structural transition temperature, implying that the local conductivity is strongly modified by the STO tetragonal domain structure. The interplay between substrate domains and the interface provides an additional mechanism for understanding and controlling the behaviour of heterostructures.

cond-mat.mtrl-sci↗

arXiv2013

Tunable Coupling of Two-Dimensional Superconductors in Bilayer SrTiO3 Heterostructures

Interlayer coupling effects between high mobility two-dimensional superconductors are studied in bilayer delta-doped SrTiO3 heterostructures. By tuning the undoped SrTiO3 spacer layer between the dopant planes, clear tunable coupling is demonstrated in the variation of the sheet carrier density, Hall mobility, superconducting transition temperature, and the temperature- and angle-dependences of the superconducting upper critical field. Systematic variation is found between one effective (merged) two-dimensional superconductor to two decoupled two-dimensional superconductors. In the intermediate coupled regime, a crossover is observed due to coupling arising from inter-sub-band interactions.

cond-mat.supr-con↗

arXiv2013

Hot electron transport in a strongly correlated transition metal oxide

Oxide heterointerfaces are ideal for investigating strong correlation effects to electron transport, relevant for oxide-electronics. Using hot-electrons, we probe electron transport perpendicular to the La$_{0.7}$Sr$_{0.3}$MnO$_{3}$ (LSMO)- Nb-doped SrTiO$_3$ (Nb:STO) interface and find the characteristic hot-electron attenuation length in LSMO to be 1.48 $\pm$ 0.10 unit cells (u.c.) at -1.9 V, increasing to 2.02 $\pm$ 0.16 u.c. at -1.3 V at room temperature. Theoretical analysis of this energy dispersion reveals the dominance of electron-electron and polaron scattering. Direct visualization of the local electron transport shows different transmission at the terraces and at the step-edges.

cond-mat.mtrl-sci↗

arXiv2012

Critical thickness for ferromagnetism in LaAlO3/SrTiO3 heterostructures

In heterostructures of LaAlO3 (LAO) and SrTiO3 (STO), two nonmagnetic insulators, various forms of magnetism have been observed [1-7], which may [8, 9] or may not [10] arise from interface charge carriers that migrate from the LAO to the interface in an electronic reconstruction [11]. We image the magnetic landscape [5] in a series of n-type samples of varying LAO thickness. We find ferromagnetic patches that appear only above a critical thickness, similar to that for conductivity [12]. Consequently we conclude that an interface reconstruction is necessary for the formation of magnetism. We observe no change in ferromagnetism with gate voltage, and detect ferromagnetism in a non-conducting p-type sample, indicating that the carriers at the interface do not need to be itinerant to generate magnetism. The fact that the ferromagnetism appears in isolated patches whose density varies greatly between samples strongly suggests that disorder or local strain induce magnetism in a population of the interface carriers.

cond-mat.str-el↗