arXiv2024

Structural analysis and transport properties of [010]-tilt grain boundaries in Fe(Se,Te)

Understanding the nature of grain boundaries is a prerequisite for fabricating high-performance superconducting bulks and wires. For iron-based superconductors [e.g. Ba(Fe,Co)$_2$As$_2$, Fe(Se,Te), and NdFeAs(O,F)], the dependence of the critical current density $J_\mathrm{c}$ on misorientation angle ($\theta_\mathrm{GB}$) has been explored on [001]-tilt grain boundaries, but no data for other types of orientations have been reported. Here, we report on the structural and transport properties of Fe(Se,Te) grown on CeO$_2$-buffered symmetric [010]-tilt roof-type SrTiO$_3$ bicrystal substrates by pulsed laser deposition. X-ray diffraction and transmission electron microscopy revealed that $\theta_\mathrm{GB}$ of Fe(Se,Te) was smaller whereas $\theta_\mathrm{GB}$ of CeO$_2$ was larger than that of the substrate. The difference in $\theta_\mathrm{GB}$ between the CeO$_2$ buffer layer and the substrate is getting larger with increasing $\theta_\mathrm{GB}$. For $\theta_\mathrm{GB}\geq24^\circ$ of the substrates, $\theta_\mathrm{GB}$ of Fe(Se,Te) was zero, whereas $\theta_\mathrm{GB}$ of CeO$_2$ was continuously increasing. The inclined growth of CeO$_2$ can be explained by the geometrical coherency model. The $c$-axis growth of Fe(Se,Te) for $\theta_\mathrm{GB}\geq24^\circ$ of the substrates is due to the domain matching epitaxy on (221) planes of CeO$_2$. Electrical transport measurements confirmed no reduction of inter-grain $J_\mathrm{c}$ for $\theta_\mathrm{GB}\leq9^\circ$, indicative of strong coupling between the grains.

cond-mat.supr-con↗

arXiv2022

K-doped Ba122 epitaxial thin film on MgO substrate by buffer engineering

Molecular beam epitaxy of K-doped Ba122 (Ba$_{1-x}$K$_x$Fe$_\text{2}$As$_\text{2}$) superconductor was realized on a MgO substrate. Microstructural observation revealed that the undoped Ba122 served as a perfect buffer layer for epitaxial growth of the K-doped Ba122. The film exhibited a high critical temperature of 39.8 K and a high critical current density of 3.9 MA/cm$^\text{2}$ at 4 K. The successful growth of epitaxial thin film will enable artificial single grain boundary on oxide bicrystal substrates and reveal the grain boundary transport nature of K-doped Ba122.

cond-mat.supr-con↗

arXiv2021

Nanoscale Texture and Microstructure in NdFeAs(O,F)/IBAD-MgO Superconducting Thin Film with Superior Critical Current Properties

This paper reports the nanoscale texture and microstructure of a high-performance NdFeAs(O,F) superconducting thin film grown by molecular beam epitaxy on a textured MgO/Y$_2$O$_3$/Hastelloy substrate. The NdFeAs(O,F) film forms a highly textured columnar grain structure by epitaxial growth on the MgO template. Although the film contains stacking faults along the $ab$-plane as well as grain boundaries perpendicular to the $ab$-plane, good superconducting properties are measured: a critical temperature, $T _{\rm c}$, of 46 K and a self-field critical current density, $J_{\rm c}$, of $2 \times 10^6 \,{\rm A/cm^2}$ at 4.2 K. Automated crystal orientation mapping by scanning precession electron diffraction in transmission electron microscopy is employed to analyze the misorientation angles between adjacent grains in a large ensemble (247 grains). 99% of the grain boundaries show in-plane misorientation angles ($Δγ$) less than the critical angle $θ_{\rm c}$, which satisfies one of the necessary conditions for the high $J_{\rm c}$. Comparing the columnar grain size distribution with the mean distance of the flux line lattice, the triple junctions of low-angle grain boundaries are found to be effective pinning centers, even at high temperatures ($\ge$35 K) and/or low magnetic fields.

cond-mat.supr-con↗

arXiv2021

Approaching the ultimate superconducting properties of (Ba,K)Fe2As2 by naturally formed low-angle grain boundary networks

The most effective way to enhance the dissipation-free supercurrent in presence of magnetic field for type II superconductors is the introduction of defects that acts as artificial pinning centres (APCs) for the vortices. For instance, the in-field critical current density of doped BaFe2As2 (Ba122), one of the most technologically important Fe-based superconductors, has been improved over the last decade by APCs created by ion-irradiation. The technique of ion-irradiation has been commonly implemented to determine the ultimate superconducting properties. However, this method is rather complicated and expensive. Here, we report on a surprisingly high critical current density and strong pinning efficiency close to the crystallographic c-axis for a K-doped Ba122 epitaxial thin film without APCs, achieving performance comparable to ion-irradiated K-doped Ba122 single crystals. Microstructural analysis reveals that the film is composed of columnar grains having width around 30-60 nm. The grains are rotated around the b- (or a-) axis by 1.5 degree and around the c-axis by -1 degree, resulting in the formation of low-angle grain boundary networks. This study demonstrates that the upper limit of in-field properties reached in ion-irradiated K-doped Ba122 is achievable by grain boundary engineering, which is a simple and industrially scalable manner.

cond-mat.supr-con↗