Oxygen in diamond: thermal stability of ST1 spin centres and creation of oxygen-pair complexes

Abstract

Little is known about oxygen-related defects in diamond. Recently, the promising room-temperature spin centre named ST1 was identified as an oxygen centre, but of still unknown atomic structure and thermal stability. In this work, we report on the optically active oxygen-related centres and the conditions for their formation, using ion implantation of oxygen in various conditions of depth and fluence. More specifically, we establish the temperature formation/stability range of the ST1 centre, which has a maximum at about 1100{\deg}C and is narrower than for NV centres. In these conditions, optically detected magnetic resonance (ODMR) on small ST1 ensembles was measured with a spin readout contrast of > 20% at 300K. In cathodoluminescence, the 535 nm ST1 peak is not observed. Besides, a broad peak centred at 460 nm is measured for implantation of O$_2$ molecular ions. For an annealing temperature of 1500{\deg}C, a different centre is formed (with ZPL at 584.5 nm) with an intensity increasing with a power law 1.5 < p < 1.9 dependence from the implantation fluence. This suggests that this centre contains two oxygen atoms. Besides, a new spectral feature associated to an intrinsic defect was also observed, with four prominent lines (especially at 594nm). Finally, the thermal formation and stability of oxygen centres in diamond presented here are important for the identification of the atomic structure of defects such as the ST1 and possible O$_2$V$_x$ complex by means of ab initio calculations. Indeed, the formation energies and charge states of defect centres are easier to compute than the full energy level scheme, which to date still remains unsuccessful regarding the ST1 centre.

Explore related subjects

Keep this discovery

BibTeXRIS

Paul Neugebauer, Xinxi Huang, Chloe Newsom, Christophe Arnold, Hjørdis Martelock, Séverine Diziain, Edoardo Monnetti, Jocelyn Achard, Tobias Lühmann, Paolo Olivero, Jan Meijer, Julien Barjon, Alexandre Tallaire, Sébastien Pezzagna. 2026-01-07. Oxygen in diamond: thermal stability of ST1 spin centres and creation of oxygen-pair complexes. https://arxiv.org/abs/2601.04418

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Measuring chiral phonons

Chiral phonons are quantized vibrations where the atomic motion in a solid breaks improper rotation symmetries. In many cases, chiral phonons possess angular momenta and are therefore selective to circularly polarized light. Both fundamental and applied research efforts on chiral phonons have been gaining increasing attention owing to their importance in a variety of fields including spintronics, spin-selective chemical reactions, thermal transport, quantum information processing and biosensing, where the bi-directional spin-lattice coupling enabled by chiral phonons can be harnessed in new ways, and potentially lead to new functionalities. Thus far, the studies of chiral phonons across diverse materials platforms have evolved largely independently within these fields, but the experimental techniques are often interrelated. In this perspective, we present a detailed description, as well as advantages and disadvantages of the current approaches for experimentally measuring chiral phonons in chiral and achiral materials. We conclude with a discussion of new methods for measuring chiral phonons. Ultimately, this work seeks to offer an experimental guide for systematically investigating the properties of chiral phonons in various materials systems and applications.

cond-mat.mtrl-sci

A model of grain growth in UN integrating molecular dynamics, phase-field modeling, and uncertainty quantification

Grain growth kinetics and grain-boundary (GB) properties in uranium mononitride (UN) are investigated through an integrated multiscale framework combining molecular dynamics (MD), phase-field modeling, and surrogate-assisted uncertainty quantification. MD simulations yield GB energies for 27 symmetric tilt boundaries from 0--2000~K, which are consistent with available DFT values. The average GB energy is nearly temperature-independent below 1000~K and increases at higher temperatures. A mechanistic pore-drag model applied to the only available grain growth dataset for actinide nitrides yields a mobility reduction factor of $s \approx 0.93$--$0.99$, statistically indistinguishable from unity, confirming that pore drag is negligible under the experimental conditions. The intrinsic GB mobility is therefore extracted directly from the effective mobility, yielding $M_0 = 2.05\times10^{-15}$~m$^4$/(J$\cdot$s) and $Q_M = 0.89$~eV. Phase-field simulations conducted from 1500--2000~K confirm normal curvature-driven grain growth, with grain size distributions converging to the Hillert-like form. A surrogate-assisted global sensitivity analysis---combining principal component analysis, Gaussian process regression, and Sobol decomposition---reveals that the mobility prefactor $M_0$ dominates output variance at all times, followed by the activation energy $Q_M$, while the GB energy $\gamma$ contributes minimally. These results establish the first quantitative grain growth framework for UN and identify the reduction of uncertainty in $M_0$ and $Q_M$ as the highest-priority target for future experimental efforts.

cond-mat.mtrl-sci

Silicon Solar Cell Design for >30% Efficiency via Singlet Fission

Singlet fission (SF) materials convert high-energy photons into multiple charge carriers, providing a route to exceed the efficiency limits of single-junction silicon solar cells without many of the complexities of multi-junction tandem designs. Following the first demonstration of an SF-enhanced silicon solar cell in 2025, there is a need to understand how SF materials can be effectively integrated into high-efficiency industrial silicon devices and translated from proof of concept to a manufacturable technology. Using coupled optical and electrical simulations, we assess the efficiency potential of several industrially relevant silicon cell architectures combined with SF materials. Interdigitated back-contact (IBC) cells offer the greatest potential for improvement due to unrestricted front-surface access and can achieve efficiencies exceeding 33%. However, performance is highly sensitive to front-surface passivation quality. Appropriate silicon design, particularly controlled surface doping and fixed interfacial charge, can mitigate recombination losses and relax passivation requirements for ultra-thin exciton-transfer layers.

cond-mat.mtrl-sci