arXiv2013

p-type doping in CVD grown MoS2 using Nb

We report on the first demonstration of p-type doping in large area few-layer films of (0001)-oriented chemical vapor deposited (CVD) MoS2. Niobium was found to act as an efficient acceptor up to relatively high density in MoS2 films. For a hole density of 4 x 1020 cm-3 Hall mobility of 8.5 cm2V-1s-1 was determined, which matches well with the theoretically expected values. XRD and Raman characterization indicate that the film had good out-of-plane crystalline quality. Absorption measurements showed that the doped sample had similar characteristics to high-quality undoped samples, with a clear absorption edge at 1.8 eV. This demonstration of p-doping in large area epitaxial MoS2 could help in realizing a wide variety of electrical and opto-electronic devices based on layered metal dichalcogenides.

cond-mat.mtrl-sci↗

arXiv2013

Unipolar Vertical Transport in GaN/AlGaN/GaN Heterostructures

In this letter, we report on unipolar vertical transport characteristics in c-plane GaN/AlGaN/GaN heterostructures. Vertical current in heterostructures with random alloy barriers was found to be independent of dislocation density and heterostructure barrier height, and significantly higher than theoretical estimates. Percolation-based transport due to random alloy fluctuations in the ternary AlGaN is suggested as the dominant transport mechanism, and confirmed through experiments showing that non-random or digital AlGaN alloys and polarization-engineered binary GaN barriers can eliminate percolation transport and reduce leakage significantly. The understanding of vertical transport and methods for effective control proposed here will greatly impact III-nitride unipolar vertical devices.

cond-mat.mes-hall↗