arXiv2012

Effect of crystallographic anisotropy on the resistance switching phenomenon in perovskites

Resistance switching effects in metal/perovskite contacts based on epitaxial c-axis oriented Y-Ba-Cu-O (YBCO) thin films with different crystallographic orientations have been studied. Three types of Ag/YBCO junctions with the contact restricted to (i) c-axis direction, (ii) ab-plane direction, and (iii) both were designed and fabricated, and their current-voltage characteristics have been measured. The type (i) junctions exhibited conventional bipolar resistance switching behavior, whereas in other two types the low-resistance state was unsteady and their resistance quickly relaxed to the initial high-resistance state. Physical mechanism based on the oxygen diffusion scenario, explaining such behavior, is discussed.

cond-mat.mes-hall↗

arXiv2010

Studies of resistance switching effects in metal/YBa2Cu3O7-x interface junctions

Current-voltage characteristics of planar junctions formed by an epitaxial c-axis oriented YBa2Cu3O7-x thin film micro-bridge and Ag counter-electrode were measured in the temperature range from 4.2 K to 300 K. A hysteretic behavior related to switching of the junction resistance from a high-resistive to a low-resistive state and vice-versa was observed and analyzed in terms of the maximal current bias and temperature dependence. The same effects were observed on a sub-micrometer scale YBa2Cu3O7-x thin film - PtIr point contact junctions using Scanning Tunneling Microscope. These phenomena are discussed within a diffusion model, describing an oxygen vacancy drift in YBa2Cu3O7-x films in the nano-scale vicinity of the junction interface under applied electrical fields.

cond-mat.mes-hall↗

arXiv2005

Nanogranular MgB2 thin films on SiC buffered Si substrates prepared by in-situ method

MgB2 thin films were deposited on SiC buffered Si substrates by sequential electron beam evaporation of B-Mg bilayer followed by in-situ annealing. The application of a SiC buffer layer enables the maximum annealing temperature of 830 C. The Transmission Electron Microscopy analysis confirms the growth of a nanogranular MgB2 film and the presence of a Mg2Si compound at the surface of the film. The 150-200 nm thick films show a maximum zero resistance critical temperature TC0 above 37 K and a critical current density JC ~ 106 A/cm2 at 11K.

cond-mat.supr-con↗

arXiv2004

Electrical and structural properties of MgB2 films prepared by sequential deposition of B and Mg on the NbN buffered Si(100) substrate

We introduce a simple method of an MgB2 film preparation using sequential electron-beam evaporation of B-Mg two-layer (followed by in-situ annealing) on the NbN buffered Si(100) substrate. The Transmission Electron Microscopy analyses confirm a growth of homogeneous nanogranular MgB2 films without the presence of crystalline MgO. A sensitive measurement of temperature dependence of microwave losses shows a presence of intergranular weak links close the superconducting transition only. The MgB2 films obtained, about 200 nm thick, exhibit a maximum zero resistance critical temperature of 36 K and critical current density of 3x10^7 A/cm^2 at 13.2 K

cond-mat.supr-con↗