Interfacial electrical and chemical properties of deposited SiO2 layers in lateral implanted 4H-SiC MOSFETs subjected to different nitridations

Abstract

In this paper, SiO2 layers deposited on 4H-SiC and subjected to different post deposition annealing (PDA) in NO and N2O were studied to identify the key factors influencing the channel mobility and threshold voltage stability in 4H-SiC MOSFETs. In particular, PDA in NO gave a higher channel mobility (55 cm2V-1s-1) than PDA in N2O (20 cm2V-1s-1), and the subthreshold behavior of the devices confirmed a lower total amount of interface states for the NO case. This latter could be also deduced from the behavior of the capacitance-voltage characteristics of 4H-SiC MOSFETs measured in gate controlled diode configuration. On the other hand, cyclic gate bias stress measurements allowed to separate the contributions of interface states (Nit) both on the upper and bottom parts of the 4H-SiC band gap and near interface oxide traps (NIOTs) in the two oxides. In particular, it was found that NO annealing reduced the total density of charges trapped at the interface states down to 3 x 1011 cm- 2 and those trapped inside the oxide down to 1 x 1011 cm-2. Electron energy loss spectroscopy demonstrated that the reduction of these traps in the NO annealed sample is due to the lower amounts of sub-stoichiometric silicon oxide (~ 1nm) and carbon-related defects (< 1nm) at the interface, respectively. This correlation represents a further step in the comprehension of the physics of the SiO2/4H-SiC interface explaining the mobility and threshold voltage behavior of 4H-SiC MOSFETs.

Explore related subjects

Keep this discovery

BibTeXRIS

Patrick Fiorenza, Corrado Bongiorno, Filippo Giannazzo, Santi Alessandrino, Angelo Messina, Mario Saggio, Fabrizio Roccaforte. 2020-12-16. Interfacial electrical and chemical properties of deposited SiO2 layers in lateral implanted 4H-SiC MOSFETs subjected to different nitridations. https://doi.org/10.1016/j.apsusc.2021.149752

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Measuring chiral phonons

Chiral phonons are quantized vibrations where the atomic motion in a solid breaks improper rotation symmetries. In many cases, chiral phonons possess angular momenta and are therefore selective to circularly polarized light. Both fundamental and applied research efforts on chiral phonons have been gaining increasing attention owing to their importance in a variety of fields including spintronics, spin-selective chemical reactions, thermal transport, quantum information processing and biosensing, where the bi-directional spin-lattice coupling enabled by chiral phonons can be harnessed in new ways, and potentially lead to new functionalities. Thus far, the studies of chiral phonons across diverse materials platforms have evolved largely independently within these fields, but the experimental techniques are often interrelated. In this perspective, we present a detailed description, as well as advantages and disadvantages of the current approaches for experimentally measuring chiral phonons in chiral and achiral materials. We conclude with a discussion of new methods for measuring chiral phonons. Ultimately, this work seeks to offer an experimental guide for systematically investigating the properties of chiral phonons in various materials systems and applications.

cond-mat.mtrl-sci

A model of grain growth in UN integrating molecular dynamics, phase-field modeling, and uncertainty quantification

Grain growth kinetics and grain-boundary (GB) properties in uranium mononitride (UN) are investigated through an integrated multiscale framework combining molecular dynamics (MD), phase-field modeling, and surrogate-assisted uncertainty quantification. MD simulations yield GB energies for 27 symmetric tilt boundaries from 0--2000~K, which are consistent with available DFT values. The average GB energy is nearly temperature-independent below 1000~K and increases at higher temperatures. A mechanistic pore-drag model applied to the only available grain growth dataset for actinide nitrides yields a mobility reduction factor of $s \approx 0.93$--$0.99$, statistically indistinguishable from unity, confirming that pore drag is negligible under the experimental conditions. The intrinsic GB mobility is therefore extracted directly from the effective mobility, yielding $M_0 = 2.05\times10^{-15}$~m$^4$/(J$\cdot$s) and $Q_M = 0.89$~eV. Phase-field simulations conducted from 1500--2000~K confirm normal curvature-driven grain growth, with grain size distributions converging to the Hillert-like form. A surrogate-assisted global sensitivity analysis---combining principal component analysis, Gaussian process regression, and Sobol decomposition---reveals that the mobility prefactor $M_0$ dominates output variance at all times, followed by the activation energy $Q_M$, while the GB energy $\gamma$ contributes minimally. These results establish the first quantitative grain growth framework for UN and identify the reduction of uncertainty in $M_0$ and $Q_M$ as the highest-priority target for future experimental efforts.

cond-mat.mtrl-sci

Silicon Solar Cell Design for >30% Efficiency via Singlet Fission

Singlet fission (SF) materials convert high-energy photons into multiple charge carriers, providing a route to exceed the efficiency limits of single-junction silicon solar cells without many of the complexities of multi-junction tandem designs. Following the first demonstration of an SF-enhanced silicon solar cell in 2025, there is a need to understand how SF materials can be effectively integrated into high-efficiency industrial silicon devices and translated from proof of concept to a manufacturable technology. Using coupled optical and electrical simulations, we assess the efficiency potential of several industrially relevant silicon cell architectures combined with SF materials. Interdigitated back-contact (IBC) cells offer the greatest potential for improvement due to unrestricted front-surface access and can achieve efficiencies exceeding 33%. However, performance is highly sensitive to front-surface passivation quality. Appropriate silicon design, particularly controlled surface doping and fixed interfacial charge, can mitigate recombination losses and relax passivation requirements for ultra-thin exciton-transfer layers.

cond-mat.mtrl-sci